- Polymer Property : Melt Flow = 8.0 g/10 min
Polymer Property : Melt Flow = 8.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | (Condition L) ASTM D-1238-94a |
| Multibase Multi-Flex® TPO 4308 BLK Data provided by Multibase. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products P250-00UV Polypropylene Copolymer, UV Stabilized, Natural Applications: ConsolesConsumer goodsInterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products P250-247 Polypropylene Copolymer, UV Stabilized, Black Applications: Center consolesInterior trimI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products P251-00 Polypropylene Copolymer, Natural Applications: Fuse panel coversCenter consolesDoor panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products P256-00 Polypropylene Copolymer, Natural Applications: Door/trunk scuffUnderhood componentsSplash shieldsElectrical enclosuresInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 210 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 410 °F |
|
| Noltex Soarnol® D2908 Ethylene Vinyl Alcohol Copolymer Ethylene content 29 mol%. Volatile matter 0.3%.The gas barrier property of Soarnol is about forty times better than that of nylon, therefore, Soarnol allows design of lower cost packages by using a.. |
|||
| Melt Flow | 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| PTS Tristar® PC-10FR-(V8) 8 MFI Flame Retardant, UV Stabilized Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| LG Chemical PI642G ABS, General Purpose, High Modulus Feature: Extrusion Molding, General Purpose, High ModulusApplication: Pipe fittingCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Inno-Comp INNOPOL® CS 1-3120 N DEL 20% Talc Filled Polypropylene Homopolymer INNOPOL® CS 1-3120 B DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Lucobit Lucofin® 1410 Polyolefin TPO Granules, Grey Lucofin is a colored, highly stabilized, bitumen-free TPO raw material based on polyolefins. Lucofin products display excellent tear resistance, flexibility, and weathering resistance. Lucofin exhi.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| SABIC Innovative Plastics Valox® V9280LW PET (Europe-Africa-Middle East) 40% Glassfiber / Mineral Filled PET, Impact Modifier, Mold Release, Heat StabilizedThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| SABIC Innovative Plastics XYLEX X7507 PC+POLYESTER (Asia Pacific) F-1 weathering certified in natural color, specially designed for Pool & Spa applications. Currently available in natural color only. |
|||
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Styrolution Novodur® H604 ABS Novodur H604 is a high heat injection molding grade with enhanced chemical resistance, especially suitable for being painted.Information provided by Styrolution |
|||
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Styrolution Novodur® H701 ABS Novodur H701 is an injection molding grade of ABS with heat resistance and high impact strength.Information provided by Styrolution |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis BorPURE™ RD266CF Polypropylene Random Copolymer BorPure™ RD266CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: BorPure™ RD266CF is recommended for
food packaging.. |
|||
| Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFPP-40 40% Glass-Reinforced Polypropylene Polifil® GFPP series compounds are homopolymer polypropylene resins reinforced with glass fibers. They provide high impact with increased strength, stiffness, surface hardness, and higher continuou.. |
|||
| Melt Flow | 8.0 - 12 g/10 min | 8.0 - 12 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® M-40 40% Mica-Reinforced Polypropylene Polifil® M series compounds are homopolymer polypropylene resins reinforced with mica. They combine an improved range of high-stiffness values with low mold shrinkage. These compounds are used in l.. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYBATCH™ U-7000-HS Blowing Agent Concentrate Based In HIPS DescriptionPOLYBATCH® U-7000-HS is a high temperature, exothermic blowing agent concentrate based in HPS.Information provided by A. Schulman. |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
| Cossa Polimeri ESTALENE EN 10 EC Modified Polyolefin Blend Formulated for injection molding or extrusion of synthetic corksCertified according to FDA standardsInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 626 °F |
|
| Covestro Apec® HT KU 1-9350 High-Heat Polycarbonate Transparent and opaque shades possible.Applications: Medical sector: superheated steam sterilization.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Entec Hypro™ PP-CP8/6 Impact Copolymer, 8 Melt Flow This product is intended for use in injection molding applications for automotive and consumer products and also contains a long-term heat aging additive package.Information provided by Entec |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
| Arkema Group Orgalloy® RS 6000 Nylon 6 Alloy, Rigid Grade (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem KN-501 Impact Copolymer Polypropylene Description: Excellent color and processing stability, excellent long term heat aging properties, wet / dry environment resistance.Applications: Suggested uses include automotive, housewares, toys, .. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Buckeye Polymers BP RPP 2508 T Polypropylene, 25% Mineral Filled This Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistance, and resis.. |
|||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | Cond. 300/1.2 ASTM D1238 |
| Ashley Polymers Ashlene® 1061R Polycarbonate A general purpose polycarbonate, low melt flow for injection molding.Data provided by the manufacturer |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Aaron Industries AAROPRENE® TFIPP 2010 High Impact Talc Filled Polypropylene AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
| DSM Arnitel® CM551 TPC-ES Heat Resistant Copolyester |
|||
| Melt Flow | 8.0 - 12 g/10 min @Load 2.16 kg, Temperature 280 °C |
8.0 - 12 g/10 min @Load 4.76 lb, Temperature 536 °F |
ASTM D1238 |
| E-Polymers EFLEX® M200 Ethylene Propylene Rubber M-series: E-FLEX M series resins are a maleic anhydride grafted (MAH) polymer concentrate designed as synthetic rubber and polyolefin manufactured by E-Polymers. It offers excellent adhesion to nyl.. |
|||
| Melt Flow | 8.0 - 11 g/10 min | 8.0 - 11 g/10 min | |
| Ashley Polymers Ashlene® RH190 Acetal General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. Available in Natural and Black. Natural: Designated RH190N-3; Black: Designated RH190B.Data provid.. |
|||