Polymer Property : Flexural Strength = 95.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	>= 95.0 MPa	>= 13800 psi	ISO 178
Polycasa PC QUINN PC sheets have excellent optical properties and a brilliant surface. The QUINN PC range contains sheets that are easy to fabricate and show exceptional performance at both low and high tempera..
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
Premix Premi-Glas® 1200H-15 Polyester SMC Premi-Glas® 1200H-15 is a 15% fiberglass-reinforced, thermoset, Sheet Molding Compound designed for applications where good arc resistance and dielectric strength are required and UL 94 HB flame re..
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
Premix Premi-Glas® 1240-15 Fiberglass Reinforced Thermoset Thick Molding Compound Premi-Glas® 1240-15 is a fiberglass reinforced thermoset Thick Molding Compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st..
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
Premix Premi-Glas® 2206-15 CR-SX Fiberglass Reinforced Thermoset SMC Premi-Glas® 2206-15 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant and HVAC applications.Key features and benefits are:Non-Halogen FR technology f..
Flexural Strength	<= 95.0 MPa	<= 13800 psi	ISO 178
Polykemi AB POLYblend 50LG PC/ABS-Blend, Low Gloss Information provided by Polykemi AB
Flexural Strength	<= 95.0 MPa	<= 13800 psi	ISO 178
Polykemi AB POLYblend 65FS PC/ABS-Blend Information provided by Polykemi AB
Flexural Strength	<= 95.0 MPa	<= 13800 psi	ISO 178
Polykemi AB POLYblend 85VB PC/ABS-Blend, Flame Retardant Information provided by Polykemi AB
Flexural Strength	<= 95.0 MPa	<= 13800 psi	ISO 178
Polykemi AB POLYform POM C M140 Polyoxymethylene Information provided by Polykemi AB
Flexural Strength	<= 95.0 MPa	<= 13800 psi	ISO 178
Polykemi AB SCANTEC PC 85FR Polycarbonate, Flame Retardant, Halogen Free Information provided by Polykemi AB
Flexural Strength	>= 95.0 MPa	>= 13800 psi	ASTM D790
NIZHNEKAMSKNEFTEKHIM 585 General Purpose Polystyrene Grade 585 is a high molecular weight, low melt-flow crystal polystyrene. This polymer is tailored for extruded foam applications such as egg cartons, meat trays and food service. It is also suited..
Flexural Strength	95.0 MPa	13800 psi	ISO 178
Radici Radilon® CS38FL (dry) Copolyamide 6 semiaromatic Film gradeInformation provided by Radici group.
Flexural Strength	95.0 MPa	13800 psi	ISO 178
Radici Radilon® CST 38FL (dry) Copolyamide 6 semiaromatic Radilon® CS can be used for blown film extrusion in general as well as being particularly suited for co-extrusion with PE because it improves the transparency and thermoformability of the film.Appl..
Flexural Strength	95.0 MPa	13800 psi	12.5 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX9610 PC (Asia Pacific) Lexan LUX9610 is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance. It intended to meet WEEE/RoHS require..
Flexural Strength	95.0 MPa	13800 psi	12.5 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX9616G PC (Asia Pacific) Lexan LUX9616G is a flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effective and thin wall FR performance. It intended to meet WEEE/RoHS requirem..
Flexural Strength	95.0 MPa	13800 psi	2 mm/min; ISO 178
Hexion Bakelite™ PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof, UL Listed (disc Phenolic molding compound, inorganically/organically filled, average heat resistance, increased dimensional stability, dish washer proof, UL listed molding compound 1.5 mm/V-0 (ALL).Application area..
Flexural Strength	95.0 MPa	13800 psi
Lehmann & Voss LUVOCOMÂ® 1700-8541 PPO, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Isotropic shrinkage characteristics.Superheated steam sterilizable.Infor..
Flexural Strength	95.0 MPa	13800 psi
Lehmann & Voss LUVOCOMÂ® 80-8510 Polyacetal-copolymer, with mineral filler, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..
Flexural Strength	95.0 MPa	13800 psi	1.5 mm/min; ISO 178:2001
Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Flexural Strength	95.0 MPa	13800 psi	conditioned, 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 115 DUS008 000000 Nylon 6, 15% Glass Fiber PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS.
Flexural Strength	95.0 MPa	13800 psi	2mm/min; ISO 178
Teijin Multilon TN-7500 Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has excellently high flowability, i.e., suitable for a large-scale business machine chassis.Information provided by T..
Flexural Strength	95.0 MPa	13800 psi	2mm/min; ISO 178
Teijin PanliteÂ® G-3330M Isotropic, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 30 % of special GF and least anisotropy grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPrecisio..
Flexural Strength	95.0 MPa	13800 psi	2mm/min; ISO 178
Teijin PanliteÂ® L-1225ZL100 Transparent and Weather Resistant grade Polycarbonate Resin Conforms to SAE regulations. It is a thin wall injection molding grade as it has high fluidity, weather resistance and mold release property and is bluish-tinted to exhibit clear color.Applications:..
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer LNP* STAT-KON* KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Flexural Strength	95.0 MPa	13800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Europe-Africa-Middle East) NORYL GFN1 is a standard 10 % glass fibre reinforced material with a HDT/A of 110C according ISO 75. NORYL GFN1 can be used for all applications where a higher modulus is required. NORYL GFN1 is ava..
Flexural Strength	95.0 MPa	13800 psi	ISO 178-93
Wellman Wellamid® 42LH-XE-NBK1 Nylon 6, Engineering Grade All information provided by Wellman Engineered Resins.
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
Polyram RamSter PF340S6 PBT, 30% Glass Beads 30% Glass beads reinforced PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	95.0 MPa	13800 psi	ISO Data
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Flexural Strength	95.0 MPa	13800 psi	ISO 178
Ascend Performance Materials Vydyne® 22HSP NT Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaAdditive: Lubricant Features:Fast Molding CycleGasoline ResistanceGeneral PurposeGood Abrasion ResistanceGood Chemical ResistanceGood Mold ReleaseGood Tou..
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
Ashley Polymers Ashlene® P1053R Polycarbonate A high flow transparent polycarbonate with good impact properties containing UV stabilizer.Data provided by the manufacturer
Flexural Strength	95.0 MPa	13800 psi	ISO 178
SABIC Innovative Plastics NORYL ENG265 PPE+PS PPE+PS blend. Unfilled. Suitable for profile extrusion. NSF listed for potable water use in several colors (Standard 61). Low water absorption. Hydrolytic stability. Dimensional stability. Typical a..