Polymer Property : Tensile Strength, Yield = 4060 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	28.0 MPa	4060 psi	50 mm/min; ASTM D638
Ovation Polymers Opnyl OP6MT254 Nylon 6 Nylon 6 – Mighty Tough plasticized extrusion grade for tubing/profile applications. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are p..
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527
Premix Thermoplastics PRE-ELEC® ESD 5300 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 5300 is a static dissipative thermoplastic compound based on polypropylene homopolymer. The dissipative property is permanent and built into the polymer chain. Surface resistance valu..
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527
Quadrant EPP Cesticolor™ HD 500 Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
Tensile Strength, Yield	28.0 MPa	4060 psi	50 mm/min; ASTM D638
NOVA Chemicals Novapol® HB-W555-AC PE Blow Molding Resin High molecular weight, High rigidity, Excellent impact strength, Excellent ESCR, Used in high purity chemical packagingInformation provided by NOVA Chemicals.
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527
SABIC Innovative Plastics LNP COLORCOMP M1000S PP LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized.
Tensile Strength, Yield	28.0 MPa	4060 psi	2.0 in/min; ASTM D638
Ineos Nova 240 High Performance Styrenic Enhanced Polystyrene (discontinued **) Extremely high impact with good flexural stiffness, Custom colorsApplications: Injection molding, Small appliances, Photographic equipmentPerformance grades of polystyrene are engineered to have spe..
Tensile Strength, Yield	28.0 - 93.1 MPa	4060 - 13500 psi	Average value: 42.8 MPa Grade Count:146
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded". Each property range of values reported is ..
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527-2
Total Lacqtene® 2005 TN 59 HDPE pipe (discontinued **) LACQTENE® 2005 TN 59 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2005 TN 59 is best processed between 190 and 230°C.Informa..
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D882
Honeywell Capran® 518 LL Heat Stabilized Nylon Film (discontinued **) Description: Capran® 518 LL is a green tinted, heat-stabilized blown film produced from low lactam nylon-6 resin. It is recommended as bagging film for advanced composite fabrication and other hig..
Tensile Strength, Yield	28.0 MPa	4060 psi
LyondellBasell LupolenÂ® 5621 D HDPE Data was collected by ISO methods and originally provided by BASF. The LupolenÂ® product line is now produced by Basell.
Tensile Strength, Yield	>= 28.0 MPa	>= 4060 psi
Kazanorgsintez PE2NT22-12 High Density Polyethylene Composite Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended for injection molding processin..
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
IRPC Polimaxx Polene 2300LC Polypropylene Block Copolymer CHARACTERISTICS: HIGH IMPACTAPPLICATIONS: INJECTION MOLDING FOR FURNITURES, HOUSEWARES, CLOSURES, CONTAINERS, CRATES, AUTOPARTS AND ELECTRICAL APPLIANCES
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527
Iran Petrochemical (PCC) BL 3VD HH 4765 High Density Polyethylene BL3VD is a high density polyethylene with 1-Butene as co monomer. It is very high density and stiffness, good ESCR, high flowability and impact strength.Applications: small blow molding, bottles, c..
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
LyondellBasell Astryn BA16G Polypropylene Copolymer Key Features: fractional melt flow, medium modulus, UV-stabilized, extrusion grade polypropylene copolymer, good flexibility, high impact strength, good colorability, good processability, good weath..
Tensile Strength, Yield	28.0 MPa	4060 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Europe-Africa-Middle East) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722.
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527
Styrolution PS 641F HIPS Styrolution PS 641F is high impact polystyrene with high heat resistance.High impactHigh heat resistanceInformation provided by Styrolution
Tensile Strength, Yield	28.0 MPa	4060 psi	50 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East) LNP* STARFLAM* MX96070 is a compound based on Polypropylene resin containing Flame Retardant. Added features include: Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middl..
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
A. Schulman POLYFORT™ FPP 3707 CAC03 Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 3707 is a 20% CAC03 filled homopolymer polypropylene product.Information provided by A. Schulman.
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
Total PPC 4252 Polypropylene, Impact Copolymer Corrugated Sheet TOTAL Petrochemicals Polypropylene 4252 is a 1.5 melt flow rate impact copolymer designed for improved toughness and high melt strength. This resin offers outstanding processability in combination ..
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene DescriptionPolyflam® RPP 1360 is a UL 94 V0 rated, non-halogenated homopolymer polypropylene flame retardant compound. Information provided by A. Schulman.
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527-2
Tisan TISOPLEN® 30% Calcite Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
Entec Hypro™ PP-CP0.5/10 Impact Copolymer, Fractional Melt Flow This is a high impact copolymer intended for use in blow molding, pipe, tubing, sheet and other extrusion applications.Information provided by Entec
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
Braskem CP 145 Injection Molding Polypropylene Applications: Household; thin-walled parts; easy mould filling. Information provided by Braskem
Tensile Strength, Yield	28.0 MPa	4060 psi	50 mm/min
Polimeri Europa EDISTIR PD RK6223N High Impact Polystyrene (HIPS) (discontinued **) Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,M,083-12-07-23 Halogen and Antimony free, medium impact polystyrene. This grade complies at 2 mm with IEC 65-20-2 and BSI..
Tensile Strength, Yield	28.0 MPa @Thickness 6.35 mm	4060 psi @Thickness 0.250 in	ASTM D638
SABIC Innovative Plastics NORYL FN215X PPE+PS Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction.
Tensile Strength, Yield	28.0 MPa	4060 psi	50 mm/min
Eastman Tenite 358-15 CAP Cellulose Acetate Propionate (discontinued **) 15% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON MFD02 PP (Asia Pacific) LNP* Stat-kon* MFD02 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM D638
BP Amoco Acctuf® 3432 Impact Copolymer Polypropylene (discontinued **) Suggested fabrication methods: Injection moldingFeatures: Nucleated, AntistaticComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded samples.