Polymer Property : Tensile Modulus = 4.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	4.00 GPa	580 ksi	ISO 527
Polikim KESTLUB® Polyamide 6 + Lubricant Kestlub® is a special type of cast polyamide ideal for bearings. It is produced by adding lubricants to cast polyamide through special processes. It performs extremely well in bearing applications ..
Tensile Modulus	4.00 GPa	580 ksi	ISO.527 DIN.53455
Omnia Plastica Rilsan® PA6 GF - Akulon GF - at 50% RH Polyamide 6 reinforced with the addition of 30% glass fibre and graphite. The glass charge makes the material highly resistant to abrasion, compression and flexing. Akulon GF is particularly suitabl..
Tensile Modulus	4.00 GPa	580 ksi	50 mm/min; ASTM D638
Ovation Polymers RIGITRON 30530 GF Polyester, 30% Glass Reinforced Polyester – 30 % Glass Fiber Reinforced PET. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM standards. Va..
Tensile Modulus	4.00 - 4.80 GPa @Thickness 4.00 mm, Temperature 23.0 °C	580 - 696 ksi @Thickness 0.157 in, Temperature 73.4 °F	depending on color; ISO 527-2/1
PolyOne Bergamid™ A70 GK30 H Polyamide 66 (Nylon 66) Information provided by PolyOne
Tensile Modulus	4.00 GPa @Temperature 23.0 °C	580 ksi @Temperature 73.4 °F	ISO 527-2/1
PolyOne Bergamid™ AB700 UF SO Polyamide 66/6 Copolymer (Nylon 66/6) Information provided by PolyOne
Tensile Modulus	4.00 GPa	580 ksi	ISO.527 DIN.53455
Omnia Plastica PA6 GF Akulon GF - Dry Polyamide 6 reinforced with the addition of 30% glass fibre and graphite. The glass charge makes the material highly resistant to abrasion, compression and flexing. Akulon GF is particularly suitabl..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527
Victrex® PEEK 450PF Fine Powder Grade Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression molding, standard flow, FDA food contact complia..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527-1/-2
DSM Akulon® K224-HGR24 Nylon 6-30% Glass Fiber and Glass Bead Reinforced (European Grade) (Cond) (discontinue The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 1-4140 BAP 40% Talc-Filled Polypropylene Homopolymer INNOPOLÂ® CS 1-4140 B AP is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOLÂ® CS 1-4140 B AP is recommended especially for producing products, where high stif..
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer INNOPOLÂ® CS 1-5140 BLH is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOLÂ® CS 1-5140 BLH is recommended especially for producing products, where high stiffn..
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics NORYL SE1GFN1 PPE+HIPS (Europe-Africa-Middle East) Noryl* SE1GFN1 is a 10% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non..
Tensile Modulus	4.00 GPa	580 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® IQ4840 PBT+PC (Asia Pacific) Xenoy iQ4840 (PBT+PC) resin is an environmental responsible, sustainable, and low carbon footprint resin. It is a 10% mineral filled resin with high modulus and ductile (HMD) characteristics. Xen..
Tensile Modulus	4.00 GPa	580 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® X4850 PBT+PC Xenoy X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional ..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527
Styron CALIBREâ„¢ 7104-8 Polycarbonate CALIBREâ„¢ 7104-8 glass-reinforced resin offers increased modulus and improved heat distortion resistance, with minimal shrinkage. It also offers outstanding UL-94 flammability ratings. CALIBRE..
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 3268
Styron PulseÂ® 979 PC/ABS PULSEâ„¢ 979 is a high performance, 10% glass filled PC/ABS resin.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics NORYL GFN1V PPE+HIPS (Europe-Africa-Middle East) NORYL GFN1V is a 10 % glass fibre reinforced material with a HDT/A of 110C according ISO 75. NORYL GFN1V cust spec 1977 has been approved for potable water applications up to 85C by the UK WFBS acco..
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Europe-Africa-Middle East) NORYL GFN1 is a standard 10 % glass fibre reinforced material with a HDT/A of 110C according ISO 75. NORYL GFN1 can be used for all applications where a higher modulus is required. NORYL GFN1 is ava..
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W..
Tensile Modulus	4.00 GPa	580 ksi
Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix HexPly® M42 is a high performance, self extinguishing, self adhesive, tough epoxy matrix for use in primary aerospace sandwich structures. It exhibits very high impact resistance and damage toleran..
Tensile Modulus	4.00 GPa	580 ksi
Covestro Makrolon® 8025 Polycarbonate High viscosity extrusion and injection molding grade with 20% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b..
Tensile Modulus	4.00 GPa	580 ksi
Covestro Makrolon® 9415(Z) Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 10% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia..
Tensile Modulus	4.00 GPa	580 ksi
BASF Gusspolyamid® Nylon 6 (Dry As Molded) Processed by anionic polymerization of caprolactam in the presence of a catalyst and activator. Uses include semi-finished products and containers (e.g. heating oil tanks).Data was collected by ISO..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527-2
Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, Conditioned Vydyne® R515 is general-purpose, 15% glass-fiber reinforced PA66 resin. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 15% Filler by WeightAdditive:Lubricant Features..
Tensile Modulus	4.00 GPa	580 ksi	1mm/min; ISO 527
Teijin Panlite® GS-3410 Friction and Abrasion Resistant, Glass Fiber Reinforced Polycarbonate Resin GF 10% reinforced grade, meeting UL 94 V-2. It is compounded with fluorine powder to improve friction and abrasion resistance, maintaining excellent characteristics of polycarbonate resin.Applicatio..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527
Polikim KESTAMID® HS Polyamide 6, Heat Resistant Kestamid-HS® is Polikim’s cast polyamide with increased heat resistance. Thermal stabilizer additives increase thermal aging significantly. In operating temperatures over 80°C, it performs with ..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527-2
Ascend Performance Materials Vydyne® R515H Nylon 66, 15% Glass Reinforced, Conditioned Vydyne® R515H is general-purpose, heat-stabilized, hydrolysis-resistant, 15% glass-fiber reinforced PA66 resin. Available in natural it is specifically designed to maximize the retention of physica..
Tensile Modulus	4.00 GPa	580 ksi	ISO 527-1, 2
Polyplastics Duracon® GB-25 Acetal Co-polymer (POM), Low warpage, GB 25% filling DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..