- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 70.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 70.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PET 1451 PRE-ELEC PET 1451 is a conductive thermoplastic compound based on PETG. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PET 14.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PP 1383 PRE-ELEC PP 1383 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Radici Radilon® CS 35FL (dry) Nylon 6/66 Radilon® CS is a range of polyamide 6/66 copolymers obtained through the polymerization of caprolactam and hexamethylendiamine salt with adipic acid.Information provided by Radici group. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | injection molded specimen; ASTM D648 |
| Phillips Sumika Marlex® AGM-110 Reactor Thermoplastic Polyolefins, Cold Temperature Impact Resistant
(discont Applications: Automotive fascias and claddingsConsumer productsTotes and binsInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 107 °C | 158 - 225 °F | Average value: 94.4 °C Grade Count:36 |
| Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Extruded". Each property range of values reported is minimum and .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Chevron Phillips HiD® 9075 HDPE Injection Molding Resin
(discontinued **) Resin Type: linear copolymer; ASTM D3350 Classification 335540A; ASTM D4976 Classification: PE 235, A 54607Characteristics: excellent flow, moderate impact strength, good stiffness, moderate ESCR, e.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| LyondellBasell Pro-fax SD242 Polypropylene Impact Copolymer Key Features: short cycle times for high productivity, good cold impact resistance, good stiffness and impact balance, high flow ease of mold filling and minimum warpage, low odor and low taste tran.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| LyondellBasell Alathon® M5372 High Density Polyethylene ApplicationsALATHON M 5372 copolymer with narrow weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processing stability. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C @Thickness 6.40 mm |
158 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical KEYFLEX BT HB9255D Ester Type TPE Description: TPC-ET, Blow Moldable, Medium Modulus, Black ColorApplication: Air duct, Hose & TubingCAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Lotte Chemical Titan TITANPRO® SM461 Polypropylene random copolymer Titanpro® SM461 is formulated with an antiblocking and slip agents package. The base resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(a)(3)(i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON TD000 PU LNP* STAT-KON* TD000 is an unfilled compound based on Polyurethane resin. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Borealis Borecene™ RM8403 Linear Polyethylene for Rotational Molding Borecene RM8403 is a third generation linear medium density natural polyethylene for rotational molding. The narrow molecular weight distribution imparted through metallocene catalyst technology pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Borealis Daplen™ KSR4525 Polypropylene Reactor Elastomer Modified Daplen KSR4525 is a reactor elastomer modified polypropylene intended for injection molding. Daplean KSR4525 is a material with excellent impact/stiffness ratio. The grade is available in natural .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Drystar 0325 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Eastman Eastar 6763 PETG Copolyester ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Eastar DN004HF Copolyester Applications:DisplaysPersonal care and CosmeticsProduct Description: Eastar Copolyester DN004HF has excellent flow characteristics while maintaining superior mechanical properties. It is easy to p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Eastar MN210 Copolyester, Natural Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates.Applications/UsesMedical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Eastar MN211 Copolyester, Natural Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. MN211 contains a mold release.Application.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman GSP01 Copolyester for Film and Sheet Extrusion Applications:Consumer e-packaging trayElectronic packagingElectrostatic dissipative trayProduct Description: GSP01 is a clear, amorphous material. Because of its clarity, toughness and good melt s.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 35 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2/B |
| ExxonMobil HDPE HMA 025 High Density Polyethylene Resin Product Description: HMA 025 is a HDPE grade, characterized by excellent dimensional stability, impact strength and very high stiffness. Availability: Africa & Middle East, Asia Pacific and Europe A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 85.0 °C | 158 - 185 °F | ISO-R 75 Method B |
| Hippe PE 300 Polyethylene Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologicall.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow UNIVAL™ DMDD-6200 NT 7 High Density Polyethylene Resin (HDPE) Moderate swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDD-6200 NT 7 is a multipurpose polymer designed for the high speed production of blow molded containers used to package hous.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM-D648 |
| Braskem GM7746C HDPE Blow Molding Polyethylene GM7746C is a high-density polyethylene specially developed for the manufacturing of blow molding fuel tanks. It has high molar mass and excellent mechanical properties. It also shows excellent tenac.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Arkema Group Rilsan® BMV 400 TL Nylon 11 (Conditioned) Designation ISO 1874-PA11,M,18-002,ZFlexible grade for injection molding. Available color: natural. Light and heat stabilized. Plasticizing agent free.Outstanding impact strength and tear spreading .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| BASF Novolen® 3248 TC Polypropylene Easy-flowing grade containing nucleating and antistatic agents for transparent injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Braskem Green PE SGM7746C Blow Molding and Monofilament High Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Mono.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D-648 |
| Axiall UV-7160 Rigid PVC, Molding Georgia Gulf UV-7160 is a rigid vinyl injection molding compound characterized by excellent flow, toughness, heat stability, color hold and surface appearance. This combination of outstanding attri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| ExxonMobil Paxon™ BC50-100 Sheet Extrusion and Blow Molding Resin
(discontinued **) BC50-100 is a high molecular weight, high density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Information provided by ExxonMobil .. |
|||