- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 100 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 100 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANBLEND SS7 PC/ASA, UV-Resistant
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Unannealed; ISO 75-2/C |
|
Pasargad Polymer Peyvand Pasalen 3P-H3230B1 Polypropylene, 30% Mineral Filled Reinforced
Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYlux 3809S F20 PC/PBT-Blend, Glass Fiber-Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
100
°C <br>@Thickness 6.40 mm
|
212
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Kingfa LONOY 6100 Flame Retardant PC/PBT Alloy
Features:Excellent balance propertiesGood weather resistanceGood size stabilitySmooth surfaceUniform colorApplications:Injection moldingElectric and electronic partsBusiness machine cabinetGarden to..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
100
°C <br>@Thickness 6.40 mm
|
212
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical Lupox® TE5000LZ PBT+PC
Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish)CAS No. 9003-01-04, 24968-12-5 and 103598-77-2Information provide..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics NORYL SE0 PPE+HIPS (Europe-Africa-Middle East)
NORYL SE0 is an unfilled, flame retardant material with a Vicat B/120 of 130C according ISO 306. NORYL SE0 is V0 at 1.6 mm according UL94 and halogen free according VDE/DIN 472 part 815.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
100
°C <br>@Thickness 3.20 mm
|
212
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON AE006 ABS
LNP* STAT-KON* AE006 is a compound based on ABS containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
100
°C <br>@Thickness 3.20 mm
|
212
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS
LNP* STAT-LOY* N30009 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® POM CO TL10 Acetal
Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, Low Friction and CopolymerInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |
|
Techmer ES Plastiblend® TPX-HTN-000BB
Availability: North AmericaForms: Pellets Features: High Heat ResistanceInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
100
°C <br>@Thickness 6.40 mm
|
212
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Samsung Cheil Industries Infino® NH-1037 PC/ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
100
°C <br>@Thickness 6.40 mm
|
212
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Samsung Cheil Industries Infino® NH-1037 PC/ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | annealed; ISO 75-A |
|
Styron Magnumâ„¢ 3453 Acrylonitrile Butadiene Styrene (ABS)
MAGNUMâ„¢ 3453 ABS is a general purpose injection molding resin suitable for a wide range of applications.Information provided by DowThis product line was spun off from Dow Chemical to Styron in ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | annealed; ISO 75-A |
|
Styron Magnumâ„¢ 3513 Acrylonitrile Butadiene Styrene (ABS)
MAGNUMâ„¢ 3513 is a grade which combines high impact with good flowability. It is suitable for injection molding and extrusion applications.Information provided by DowThis product line was spun ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
|
Polyram PlusTek PA340S8 Nylon 6.6 for Injection Molding, 40% Glass-beads Reinforced
40% Glass-beads reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
|
Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding
General purpose polyacetal homopolymer for injection molding applications, MFI 1.7.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
DSM Arnite® TM4 440 (PBT+PET)-MD20
20% Mineral Reinforced
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® BM-30 FR PA6-MD30 FR
Information provided by EMS Grivory
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® 300CP NC010 Acetal (POM)
(Unverified Data**)
Medium-high Viscosity Acetal Homopolymer with Improved ProcessingDelrin 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of proc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-2 |
|
Denka MALECCA K-300 ABS
A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
|
Asahi Kasei Xyron® 300Z Modified Polyphenylene Ether
Flame RetardantInformation provided by Asahi Kasei
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
|
BLUESTAR BS130 Acetal Copolymer
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D-648 |
|
Plaskolite West Optix® CA - 75 UVT General Purpose Acrylic Resin
Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75/Method Af |
|
Premix Thermoplastics PRE-ELEC® ESD 12-000
(discontinued **)
PRE-ELEC ESD 12-000 is a static dissipative thermoplastic compound based on polyacetal copolymer. The dissipative property is permanent and built into the polymer chain. The products made out of PRE..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | GB/1634 |
|
Zhejiang Juner PC/ABSz-4 Alloy
Applications: Shell of Small Household Electric ApplianceInformation provided by Zhejiang Juner New Materials Co, Ltd.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
|
E-Polymers SEPAZ® N3040HR Nanoclay 3% Dimensional stability, Super Toughness Nano Composite Resin
Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
|
Ashley Polymers Ashlene® PC/ABS Alloy 305
General purpose high gloss with high impact, good low temperature properties and high heat resistance.Data provided by the manufacturer
|
|||