Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 410 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
STN EN ISO 75/A
Plastcom SLOVAMID 6 GF 60 Polyamide 6, 60% Glass Fiber
FeaturesPA 6 for injection moulding, chemically strengthened with 60% of glass fiber, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-good..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Plastcom SLOVAMID 66 Y 35 FRY 7 PA66, 35% mineral filling
FeaturesPA 66 for injection moulding, chemically reinforced with 35 % mineral filler and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 /3.2 mm/ in accordance wi..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Unannealed; ISO 75-2/A
PolyOne Bergamid™ A700 G20 UF Polyamide 66 (Nylon 66)
Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber  (discontinued **)
PBT+PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75
Nilit FRIANYL B63 FK 1010 Nylon 6 for injection molding, 10% glass fiber and 10% glass ball reinforced
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 3.18 mm
410 °F

@Thickness 0.125 in
Unannealed; ASTM D648
LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant  (discontinued **)
Office equipment internal parts.Features: Lubricated, Good Wear ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labe..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose
Feature: Injection Molding,PA6+GF30%, General PurposeApplication: Automotive (Cooling Fan)CAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical Lupox® NH2306F PBT+GF30%
Description: Injection Molding, PBT+GF30%, Halogen Free Flame RetardantApplication: IT/OA, E&E (Connector)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75/Af
Solvay TECHNYL® A 548B2 V15 PA66, 15% glass fiber, DRY
Description: TECHNYL® A 548B2 V15 is a polyamide 6.6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits: Th..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics ULTEM 2310F PEI (Europe-Africa-Middle East)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 listing. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics ULTEM 2410 PEI (Europe-Africa-Middle East)
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 3.20 mm
410 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Valox® PDR4910 PBT (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Unannealed; ASTM D648
Techmer ES HiFill® PA6 GF33 HS L 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Heat Stabilized, Good UV..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics LNP THERMOCOMP PF005 PA 6 (Europe-Africa-Middle East)
25% glass fibre reinforced Polyamide 6 injection moulding resin.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 3.20 mm
410 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics NORYL GTX GTX8410W PPE+PA
High flow, 10% Glass Reinforced PPE+PA. Typically used in Automotive connectors.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/2
Suzhou Hipro Polymers Hiprolon® 70 MC HLS G30 Nylon 610, 30% glass fiber filled
Hiprolon® 70 MC HLS G30 polyamide 6.10 compound reinforced with 30% chopped glass fiber for injection molding. Features: high heat resistance, dimension stability, impact resistance, good flow ab..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-93
Wellman Wellamid® GF33-66/6 XE-BKDX9 Nylon 66/6, 33% Glass Fiber Reinforced
Chrysler DX9 color matchedAll information provided by Wellman Engineered Resins.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Toyobo ECOVYLOPET® EMC2310 PET Bottle Recycling Grade, 10% Glass Reinforced
Features: PET Bottle Recycling Grade, 10% Glass Fiber Reinforced, General PurposeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
DuPont Performance Polymers Crastin® SK609 BK851 Polybutylene Terephthalate (PBT)  (Unverified Data**)
50% Glass Reinforced Polybutylene Terephthalate Crastin SK609 BK851 is a 50% glass fiber reinforced lubricated black polybutylene terephthalate resin for injection molding.Information provided by Du..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
DuPont Performance Polymers Crastin® SK695FR NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l
30% Glass Reinforced Flame Retardant Polybutylene Terephthalate  Crastin® SK695FR is a 30% glass reinforced flame retardant polybutylene terephthalate for injection moulding.Information provided b..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Unannealed; ASTM D648
Entec Hylox® 9030 PBT, 30% Glass Reinforced
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D648
Clariant Renol 60G33HSL Nylon 6, 33% Glass Fiber Reinforced, Heat Stabilized, Lubricated
Data provided by Clariant Masterbatches
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry)
Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM Data
BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry)  (discontinued **)
Capron 8333G HI HS BK-102 is a 33% glass reinforced, impact modified polyamide 6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in c..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 3.18 mm
410 °F

@Thickness 0.125 in
Unannealed; ASTM D648
LNP ULTEM® SMU5806 Polyetherimide, 8% Carbon Fiber Reinforcement  (discontinued **)
Features: Low ShrinkageForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still..
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Annealed, 0.125 in bars; ASTM D648
PolyOne Edgetek® ES-20GF/000 Polyethersulfone, Glass Filled  (discontinued **)
Description/Features:Glass Fiber ReinforcedInformation provided by PolyOne Corporation.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1,-2
Lanxess Pocan® BFN 4231 000000 PBT, 25% Glass Fiber
PBT, 25% glass fibers, injection molding, halogen free flame retardantInformation provided by LANXESS.
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Europe-Africa-Middle East)
Thermally conductive mineral and glass fiber filled PA6, FR, compliant with ECO protocols, non-brominated, non-chlorinated