Manufacturer : Haynes International, Inc. Product List

Category

Cobalt Alloy	Superalloy	Nickel Alloy
Iron Base	Alpha/Near Alpha Titanium Alloy

Trade Name

Hastelloy®

Multimet®

Ultimet®

Tips：100 items are displayed at most. For the rest of the results, please contact customer service.

PRODUCT NO.	Category	Trade Name
Haynes 214Â® alloy, 10% cold reduction	Superalloy
Haynes 214Â® alloy, 20% cold reduction	Superalloy
Haynes 214Â® alloy, 20% cold reduction, 1095Â°C (2000Â°F) for 5 minutes	Superalloy
Haynes 230Â® alloy, 40% cold reduction, 1177Â°C anneal for 5 minutes	Superalloy
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370Â°C (700Â°F) for 1 hour	Superalloy
Haynes HastelloyÂ® G-30Â® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire	Superalloy	Hastelloy®
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 16000 hours	Superalloy	Hastelloy®
Haynes HastelloyÂ® S alloy, gas tungsten arc welded	Superalloy	Hastelloy®
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 4000 hours	Superalloy	Hastelloy®
Haynes HastelloyÂ® S alloy, weld metal, aged 1000 hours	Superalloy	Hastelloy®
Haynes HastelloyÂ® S alloy, weld metal, aged 16000 hours	Superalloy	Hastelloy®
Haynes HastelloyÂ® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments	Superalloy	Hastelloy®
Haynes HR-120Â® alloy, solution heat-treated aged at 1400Â°F for 1000 hours	Iron Base
Haynes HR-160Â® alloy, plate, aged 8000 hours at 871Â°C (1600Â°F)	Superalloy
Haynes HR-224Â® Nickel Alloy	Nickel Alloy
Haynes MultimetÂ® alloy, 1.6 mm thick sheet, 1177Â°C heat treatment, rapid air cooled	Iron Base	Multimet®
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 5% cold reduction	Iron Base	Multimet®
Haynes UltimetÂ® alloy, aged 1000 hours at 204Â°C (400Â°F)	Superalloy	Ultimet®
Haynes Waspaloyâ„¢ alloy, sheet	Superalloy
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750)	Nickel Alloy
Haynes 230Â® alloy, plate, 8000 hours exposure at 871Â°C (1600Â°F)	Superalloy
Haynes 25 alloy, cold worked sheet, 15 % cold reduction	Superalloy
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate	Nickel Alloy
Haynes 556Â® alloy, 10% cold reduction	Iron Base
Haynes 556Â® alloy, bar, after 0 hours at 650Â°C (1200Â°F)	Iron Base
Haynes 556Â® alloy, bar, after 4000 hours at 760Â°C (1400Â°F)	Iron Base
Haynes 625 alloy, 20% cold reduction, 1010Â°C anneal for 5 minutes	Superalloy
Haynes 625 alloy, plate after 8000 hours at 760Â°C (1400Â°F)	Superalloy
Haynes 625 alloy, plate after 8000 hours at 870Â°C (1600Â°F)	Superalloy
Haynes 718 alloy, cold rolled, solution-treated and aged sheet	Superalloy
Haynes HastelloyÂ® C-2000Â® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate	Nickel Alloy	Hastelloy®
Haynes HastelloyÂ® C-2000Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform	Nickel Alloy	Hastelloy®
Haynes HastelloyÂ® C-22Â® alloy, 50% cold worked sheet	Superalloy	Hastelloy®
Haynes HastelloyÂ® C-22Â® alloy, GTAW weld, C-22 base metal, C-22 weld metal	Superalloy	Hastelloy®
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform	Nickel Alloy	Hastelloy®
Haynes HastelloyÂ® G-30Â® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire	Superalloy	Hastelloy®
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Sheet, Cold Rolled and Solution Annealed	Nickel Alloy	Hastelloy®
Haynes 25 alloy, room temperature after 15% cold reduction	Superalloy
Haynes 556® alloy, 40% cold reduction	Iron Base
Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes	Iron Base
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F)	Iron Base
Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched	Superalloy	Hastelloy®
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire	Superalloy	Hastelloy®
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C)	Nickel Alloy	Hastelloy®
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)	Superalloy	Hastelloy®
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction	Iron Base	Multimet®
Haynes 230® alloy, as cast vacuum investment casting	Superalloy
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet	Superalloy	Hastelloy®
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C)	Nickel Alloy	Hastelloy®