Axiall ProTherm® 4526 CPVC Rigid PVC, Molding
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | Axiall |
| Trade Name | PROtherm® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Axiall ProTherm® 4526 CPVC Rigid PVC, Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Georgia Gulf ProTherm® 4526 CPVC is a pelletized injection molding compound designed for fittings. Typical applications are in potable water and chemical transfer systems especially where high resistance and/or elevated temperatures exist. 4526 has excellent processability, including thermal stability, flow, and surface appearance. ProTherm® 4526 is listed under NSF Standard 14 and Standard 61 and meets or exceeds ASTM D-1784 cell class 23447-B requirements.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D-792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D-955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D-785 |
| Tensile Strength, Yield | 55.2 MPa | 8010 psi | ASTM D-638 |
| Tensile Modulus | 3.41 GPa | 495 ksi | ASTM D-638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D-790 |
| Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D-790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 6.35 mm |
2.50 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 20.3 J @Temperature 23.0 °C |
15.0 ft-lb @Temperature 73.4 °F |
1/2" R Tup, 180 mil |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106.0 °C | 222.8 °F | annealed; ASTM D-648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101.0 °C | 213.8 °F | annealed; ASTM D-648 |
| Vicat Softening Point | 100 °C | 212 °F | 5kg Load at 50°C per Hour(annealed); ASTM D-1525A |
| Oxygen Index | 44 % | 44 % | ASTM D-2863 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cell Classification, ASTM D-1784 | 23447-B | |
| Flow Ratio (Distance/Wall Thickness, 410-425°F) | 110 | Georgia Gulf Test |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PC 69 T 10 003/1M Polypropylene reinforced with mineral filler
- SABIC Innovative Plastics Lexan® HFD4211 PC
- NOVA Chemicals Novapol® PR-0636-UG Butene MDPE Rotational Molding Resin (discontinued **)
- Ensinger Sintimid™ V 40% graphite Polyimide (PI) (discontinued **)
- A. Schulman PAPERMATCH® T-4776/50 Specialty Masterbatch
- EMS-Grivory Grivory® F 34 NL PA6
- Dow Corning JCR 6109
- Braskem FH35 HDPE Cast Film Extrusion Polyethylene Copolymer
- Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes
- BP Amoco Acclear® 8649X Random Copolymer Polypropylene, High Clarity Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved