Borealis Borstar® HE6081 Black Track Resistant HD Polyethylene Based Compound for Jacketing of Fiber Optical Cable

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Extruded
Manufacturer	Borealis
Trade Name	Borstar®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Borstar® HE6081 Black Track Resistant HD Polyethylene Based Compound for Jacketing of Fiber Optical Cable.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Borstar HE6081 is based on high-density polyethylene and has a specially designed additive package to give excellent track resistance. It is also well protected against UV degradation in order to ensure outstanding weathering applications. Borstar HE6081 is developed for jacketing of Fiber Optical cables designed for installation in high voltage power transmission lines. The compound may also be used for other applications where thermoplastic track resistance materials can be applied. It can resist severe installation conditions and service conditions even at elevated ambient temperatures.Information provided by the Manufacturer.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ASTM D1505
ESCR 10% Igepal®	>= 2000 hour	>= 2000 hour	ASTM D1693
Melt Flow	0.40 g/10 min @Load 2.16 kg	0.40 g/10 min @Load 4.76 lb	ASTM D1238
	2.0 g/10 min @Load 5.00 kg	2.0 g/10 min @Load 11.0 lb	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	59	59	ASTM D2240
Tensile Strength at Break	25.0 MPa @Temperature 0.000 °C	3630 psi @Temperature 32.0 °F	ASTM D638
	25.0 MPa @Temperature -30.0 °C	3630 psi @Temperature -22.0 °F	ASTM D638
Tensile Strength, Ultimate	11.0 MPa @Temperature 70.0 °C	1600 psi @Temperature 158 °F	ASTM D638
Tensile Strength, Yield	6.89 MPa @Temperature 70.0 °C	1000 psi @Temperature 158 °F	ASTM D638
	25.0 MPa @Temperature 0.000 °C	3630 psi @Temperature 32.0 °F	ASTM D638
	30.0 MPa @Temperature -30.0 °C	4350 psi @Temperature -22.0 °F	ASTM D638
Elongation at Break	200 % @Temperature -30.0 °C	200 % @Temperature -22.0 °F	ASTM D638
	400 % @Temperature 0.000 °C	400 % @Temperature 32.0 °F	ASTM D638
	500 % @Temperature 70.0 °C	500 % @Temperature 158 °F	ASTM D638
Elongation at Yield	4.0 % @Temperature 0.000 °C	4.0 % @Temperature 32.0 °F	ASTM D638
	4.0 % @Temperature -30.0 °C	4.0 % @Temperature -22.0 °F	ASTM D638
	9.0 % @Temperature 70.0 °C	9.0 % @Temperature 158 °F	ASTM D638

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -80.0 °C	<= -112 °F	ASTM D746

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.5 @Frequency 50 Hz	2.5 @Frequency 50 Hz	ASTM D150
Dielectric Strength	>= 19.7 kV/mm	>= 500 kV/in	ASTM D149
Dissipation Factor	0.00020 @Frequency 50 Hz	0.00020 @Frequency 50 Hz	ASTM D150