Constellium Fortal® Aluminum Alloy

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name Fortal®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium Fortal® Aluminum Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for moulds and tools, robotics, machine housings etc.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.81 g/cc
0.102 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength >= 450 MPa

@Thickness 180 - 200 mm
 >= 65300 psi

@Thickness 7.09 - 7.87 in
>= 470 MPa

@Thickness 140 - 160 mm
 >= 68200 psi

@Thickness 5.51 - 6.30 in
>= 480 MPa

@Thickness 120 - 140 mm
 >= 69600 psi

@Thickness 4.72 - 5.51 in
>= 480 MPa

@Thickness 160 - 180 mm
 >= 69600 psi

@Thickness 6.30 - 7.09 in
>= 485 MPa

@Thickness 100 - 120 mm
 >= 70300 psi

@Thickness 3.94 - 4.72 in
>= 495 MPa

@Thickness 80.0 - 100 mm
 >= 71800 psi

@Thickness 3.15 - 3.94 in
>= 500 MPa

@Thickness 60.0 - 80.0 mm
 >= 72500 psi

@Thickness 2.36 - 3.15 in
505 MPa

@Thickness 180 - 200 mm
 73200 psi

@Thickness 7.09 - 7.87 in
 Typical Strength
510 MPa

@Thickness 160 - 180 mm
 74000 psi

@Thickness 6.30 - 7.09 in
 Typical Strength
515 MPa

@Thickness 140 - 160 mm
 74700 psi

@Thickness 5.51 - 6.30 in
 Typical Strength
520 MPa

@Thickness 120 - 140 mm
 75400 psi

@Thickness 4.72 - 5.51 in
 Typical Strength
525 MPa

@Thickness 60.0 - 80.0 mm
 76100 psi

@Thickness 2.36 - 3.15 in
 Typical Strength
530 MPa

@Thickness 100 - 120 mm
 76900 psi

@Thickness 3.94 - 4.72 in
 Typical Strength
>= 530 MPa

@Thickness 50.0 - 60.0 mm
 >= 76900 psi

@Thickness 1.97 - 2.36 in
535 MPa

@Thickness 80.0 - 100 mm
 77600 psi

@Thickness 3.15 - 3.94 in
 Typical Strength
>= 540 MPa

@Thickness 40.0 - 50.0 mm
 >= 78300 psi

@Thickness 1.57 - 1.97 in
>= 550 MPa

@Thickness 25.0 - 40.0 mm
 >= 79800 psi

@Thickness 0.984 - 1.57 in
>= 555 MPa

@Thickness 6.50 - 12.0 mm
 >= 80500 psi

@Thickness 0.256 - 0.472 in
>= 555 MPa

@Thickness 12.0 - 25.0 mm
 >= 80500 psi

@Thickness 0.472 - 0.984 in
560 MPa

@Thickness 50.0 - 60.0 mm
 81200 psi

@Thickness 1.97 - 2.36 in
 Typical Strength
570 MPa

@Thickness 40.0 - 50.0 mm
 82700 psi

@Thickness 1.57 - 1.97 in
 Typical Strength
580 MPa

@Thickness 25.0 - 40.0 mm
 84100 psi

@Thickness 0.984 - 1.57 in
 Typical Strength
590 MPa

@Thickness 6.50 - 12.0 mm
 85600 psi

@Thickness 0.256 - 0.472 in
 Typical Strength
590 MPa

@Thickness 12.0 - 25.0 mm
 85600 psi

@Thickness 0.472 - 0.984 in
 Typical Strength
Tensile Strength, Yield >= 380 MPa

@Strain 0.200 %,
Thickness 180 - 200 mm
 >= 55100 psi

@Strain 0.200 %,
Thickness 7.09 - 7.87 in
>= 390 MPa

@Strain 0.200 %,
Thickness 160 - 180 mm
 >= 56600 psi

@Strain 0.200 %,
Thickness 6.30 - 7.09 in
>= 400 MPa

@Strain 0.200 %,
Thickness 140 - 160 mm
 >= 58000 psi

@Strain 0.200 %,
Thickness 5.51 - 6.30 in
>= 405 MPa

@Strain 0.200 %,
Thickness 120 - 140 mm
 >= 58700 psi

@Strain 0.200 %,
Thickness 4.72 - 5.51 in
>= 410 MPa

@Strain 0.200 %,
Thickness 100 - 120 mm
 >= 59500 psi

@Strain 0.200 %,
Thickness 3.94 - 4.72 in
>= 415 MPa

@Strain 0.200 %,
Thickness 80.0 - 100 mm
 >= 60200 psi

@Strain 0.200 %,
Thickness 3.15 - 3.94 in
>= 420 MPa

@Strain 0.200 %,
Thickness 60.0 - 80.0 mm
 >= 60900 psi

@Strain 0.200 %,
Thickness 2.36 - 3.15 in
>= 445 MPa

@Strain 0.200 %,
Thickness 50.0 - 60.0 mm
 >= 64500 psi

@Strain 0.200 %,
Thickness 1.97 - 2.36 in
445 MPa

@Strain 0.200 %,
Thickness 60.0 - 80.0 mm
 64500 psi

@Strain 0.200 %,
Thickness 2.36 - 3.15 in
 Typical Strength
445 MPa

@Strain 0.200 %,
Thickness 180 - 200 mm
 64500 psi

@Strain 0.200 %,
Thickness 7.09 - 7.87 in
 Typical Strength
450 MPa

@Strain 0.200 %,
Thickness 160 - 180 mm
 65300 psi

@Strain 0.200 %,
Thickness 6.30 - 7.09 in
 Typical Strength
455 MPa

@Strain 0.200 %,
Thickness 140 - 160 mm
 66000 psi

@Strain 0.200 %,
Thickness 5.51 - 6.30 in
 Typical Strength
465 MPa

@Strain 0.200 %,
Thickness 120 - 140 mm
 67400 psi

@Strain 0.200 %,
Thickness 4.72 - 5.51 in
 Typical Strength
>= 470 MPa

@Strain 0.200 %,
Thickness 40.0 - 50.0 mm
 >= 68200 psi

@Strain 0.200 %,
Thickness 1.57 - 1.97 in
>= 475 MPa

@Strain 0.200 %,
Thickness 25.0 - 40.0 mm
 >= 68900 psi

@Strain 0.200 %,
Thickness 0.984 - 1.57 in
475 MPa

@Strain 0.200 %,
Thickness 100 - 120 mm
 68900 psi

@Strain 0.200 %,
Thickness 3.94 - 4.72 in
 Typical Strength
480 MPa

@Strain 0.200 %,
Thickness 80.0 - 100 mm
 69600 psi

@Strain 0.200 %,
Thickness 3.15 - 3.94 in
 Typical Strength
>= 480 MPa

@Strain 0.200 %,
Thickness 6.50 - 12.0 mm
 >= 69600 psi

@Strain 0.200 %,
Thickness 0.256 - 0.472 in
>= 480 MPa

@Strain 0.200 %,
Thickness 12.0 - 25.0 mm
 >= 69600 psi

@Strain 0.200 %,
Thickness 0.472 - 0.984 in
485 MPa

@Strain 0.200 %,
Thickness 50.0 - 60.0 mm
 70300 psi

@Strain 0.200 %,
Thickness 1.97 - 2.36 in
 Typical Strength
500 MPa

@Strain 0.200 %,
Thickness 40.0 - 50.0 mm
 72500 psi

@Strain 0.200 %,
Thickness 1.57 - 1.97 in
 Typical Strength
520 MPa

@Strain 0.200 %,
Thickness 25.0 - 40.0 mm
 75400 psi

@Strain 0.200 %,
Thickness 0.984 - 1.57 in
 Typical Strength
525 MPa

@Strain 0.200 %,
Thickness 6.50 - 12.0 mm
 76100 psi

@Strain 0.200 %,
Thickness 0.256 - 0.472 in
 Typical Strength
525 MPa

@Strain 0.200 %,
Thickness 12.0 - 25.0 mm
 76100 psi

@Strain 0.200 %,
Thickness 0.472 - 0.984 in
 Typical Strength
Elongation at Break >= 2.0 %

@Thickness 180 - 200 mm
 >= 2.0 %

@Thickness 7.09 - 7.87 in
>= 3.0 %

@Thickness 160 - 180 mm
 >= 3.0 %

@Thickness 6.30 - 7.09 in
>= 4.0 %

@Thickness 120 - 140 mm
 >= 4.0 %

@Thickness 4.72 - 5.51 in
>= 4.0 %

@Thickness 140 - 160 mm
 >= 4.0 %

@Thickness 5.51 - 6.30 in
>= 5.0 %

@Thickness 60.0 - 80.0 mm
 >= 5.0 %

@Thickness 2.36 - 3.15 in
>= 5.0 %

@Thickness 80.0 - 100 mm
 >= 5.0 %

@Thickness 3.15 - 3.94 in
>= 5.0 %

@Thickness 100 - 120 mm
 >= 5.0 %

@Thickness 3.94 - 4.72 in
5.0 %

@Thickness 160 - 180 mm
 5.0 %

@Thickness 6.30 - 7.09 in
 Typical Elongation
5.0 %

@Thickness 180 - 200 mm
 5.0 %

@Thickness 7.09 - 7.87 in
 Typical Elongation
6.0 %

@Thickness 140 - 160 mm
 6.0 %

@Thickness 5.51 - 6.30 in
 Typical Elongation
>= 6.0 %

@Thickness 25.0 - 40.0 mm
 >= 6.0 %

@Thickness 0.984 - 1.57 in
>= 6.0 %

@Thickness 40.0 - 50.0 mm
 >= 6.0 %

@Thickness 1.57 - 1.97 in
>= 6.0 %

@Thickness 50.0 - 60.0 mm
 >= 6.0 %

@Thickness 1.97 - 2.36 in
>= 7.0 %

@Thickness 12.0 - 25.0 mm
 >= 7.0 %

@Thickness 0.472 - 0.984 in
7.0 %

@Thickness 120 - 140 mm
 7.0 %

@Thickness 4.72 - 5.51 in
 Typical Elongation
8.0 %

@Thickness 60.0 - 80.0 mm
 8.0 %

@Thickness 2.36 - 3.15 in
 Typical Elongation
8.0 %

@Thickness 80.0 - 100 mm
 8.0 %

@Thickness 3.15 - 3.94 in
 Typical Elongation
>= 8.0 %

@Thickness 6.50 - 12.0 mm
 >= 8.0 %

@Thickness 0.256 - 0.472 in
8.0 %

@Thickness 100 - 120 mm
 8.0 %

@Thickness 3.94 - 4.72 in
 Typical Elongation
9.0 %

@Thickness 25.0 - 40.0 mm
 9.0 %

@Thickness 0.984 - 1.57 in
 Typical Elongation
9.0 %

@Thickness 40.0 - 50.0 mm
 9.0 %

@Thickness 1.57 - 1.97 in
 Typical Elongation
9.0 %

@Thickness 50.0 - 60.0 mm
 9.0 %

@Thickness 1.97 - 2.36 in
 Typical Elongation
10 %

@Thickness 12.0 - 25.0 mm
 10 %

@Thickness 0.472 - 0.984 in
 Typical Elongation
11 %

@Thickness 6.50 - 12.0 mm
 11 %

@Thickness 0.256 - 0.472 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
tensile