Diamond Polymers DIAMALOY 527 PC/PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers DIAMALOY 527 PC/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 26.4 g/10 min @Load 5.00 kg, Temperature 260 °C |
26.4 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | chs 2.0 in/min; ASTM D638 |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 1.95 GPa | 283 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 128 °C @Load 1.00 kg, Thickness 3.17 mm |
262 °F @Load 2.20 lb, Thickness 0.125 in |
ASTM D1527 |
Users viewing this material also viewed the following:
- Victrex® PEEK 150UF10 Polyetheretherketone
- Nilit FRIANYL B63 W-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced
- DuPont Performance Polymers Zytel® 73G30T NC010 Nylon 6 (Unverified Data**)
- Techmer ES Luriblend® PA6 GF15 TL15 15% Glass Filled
- Eurotec® Tecodur® PB70 GR30 NL100 IL PBT, 30% glass fiber reinforced, impact modified, natural
- BASF Hexamethylenediamine 70%
- E-Polymers EFLEX® S5090 Extrusion
- Radici Radilon® A RV330 (dry) Nylon 66
- S&E Specialty Polymers TufTech™ GM-93-060 PVC Compound
- Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F)
Copyright © lookpolymers.com All Rights Reserved