Dow Primacor® 1430 Ethylene Acrylic Acid (EAA)
| Category | Polymer , Film , Thermoplastic , Ethylene Acrylic Acid |
| Manufacturer | Dow Chemical |
| Trade Name | Primacor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Primacor® 1430 Ethylene Acrylic Acid (EAA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | |
| Thickness | 60.0 microns | 2.36 mil | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg |
5.0 g/10 min @Load 4.76 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | Molded property |
| Film Tensile Strength at Yield, MD | 8.10 MPa | 1170 psi | |
| Film Tensile Strength at Yield, TD | 7.90 MPa | 1150 psi | |
| Tensile Strength, Yield | 8.10 MPa | 1170 psi | Molded property |
| Film Elongation at Break, MD | 525 % | 525 % | |
| Film Elongation at Break, TD | 535 % | 535 % | |
| Elongation at Break | 545 % | 545 % | Molded value |
| Tensile Modulus | 0.124 GPa | 18.0 ksi | |
| Elmendorf Tear Strength MD | 450 g | 450 g | |
| Elmendorf Tear Strength TD | 510 g | 510 g | |
| Elmendorf Tear Strength, MD | 7.50 g/micron | 191 g/mil | |
| Elmendorf Tear Strength, TD | 8.50 g/micron | 216 g/mil | |
| Dart Drop | 6.70 g/micron | 170 g/mil | |
| Film Tensile Strength at Break, MD | 35.9 MPa | 5210 psi | |
| Film Tensile Strength at Break, TD | 35.9 MPa | 5210 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 78.0 °C | 172 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % | 3.0 % | |
| Gloss | 70 % | 70 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 191 °C | 376 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CP - 927 G High Impact Acrylic Resin
- LyondellBasell Lupolen® 3010 K LDPE, Injection Molding Grade
- Kotec Carbotex K-40MRA Polycarbonate, General Purpose, Mold Release Grade
- SABIC Innovative Plastics Valox® 8032UX PBT+PET (Europe-Africa-Middle East)
- Teknor Apex Monprene® MP-2564B Thermoplastic Elastomer
- 3M BBI-A Shrinkable Tubing for Bus Bar
- ArcelorMittal Usibor® 1500 Ultra high strength steel, Cold Rolled
- Pyrotek TS-81 Thermoset Electrical Insulation Product (Nema Grade: CE)
- Mitsubishi Xantar® MX 1004 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved