DuPont Performance Polymers Rynite® 830ER NC010 PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Rynite® 830ER NC010 PET.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Rynite® 830ER is 30% glass reinforced with excellent high temperature dielectric properties. Class H (180C).Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D792
Filler Content 30 %
30 %
Water Absorption 0.060 %
<br>@Temperature 23.0 °C
 0.060 %
<br>@Temperature 73.4 °F
 50%RH,23°C,24h; ASTM D570
0.060 %
<br>@Thickness 1.00 mm,<br> Temperature 23.0 °C
 0.060 %
<br>@Thickness 0.0394 in,<br> Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
Linear Mold Shrinkage 0.0013 cm/cm
<br>@Thickness 1.57 mm
 0.0013 in/in
<br>@Thickness 0.0618 in
 Flow; ASTM D955
0.0015 cm/cm
<br>@Thickness 3.20 mm
 0.0015 in/in
<br>@Thickness 0.126 in
 Flow; ASTM D955
0.0060 cm/cm
<br>@Thickness 1.57 mm
 0.0060 in/in
<br>@Thickness 0.0618 in
 Transverse; ASTM D955
0.0070 cm/cm
<br>@Thickness 3.20 mm
 0.0070 in/in
<br>@Thickness 0.126 in
 Transverse; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ASTM D785
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 165 MPa
<br>@Temperature 23.0 °C
 23900 psi
<br>@Temperature 73.4 °F
 ISO 527
Tensile Strength 68.0 MPa
<br>@Temperature 150 °C
 9860 psi
<br>@Temperature 302 °F
 ASTM D638
107 MPa
<br>@Temperature 93.0 °C
 15500 psi
<br>@Temperature 199 °F
 ASTM D638
169 MPa
<br>@Temperature 23.0 °C
 24500 psi
<br>@Temperature 73.4 °F
 ASTM D638
193 MPa
<br>@Temperature -40.0 °C
 28000 psi
<br>@Temperature -40.0 °F
 ASTM D638
Elongation at Break 2.1 %
<br>@Temperature -40.0 °C
 2.1 %
<br>@Temperature -40.0 °F
 ASTM D638
2.3 %
<br>@Temperature 23.0 °C
 2.3 %
<br>@Temperature 73.4 °F
 ASTM D638
2.3 %
<br>@Temperature 23.0 °C
 2.3 %
<br>@Temperature 73.4 °F
 ISO 527
3.6 %
<br>@Temperature 93.0 °C
 3.6 %
<br>@Temperature 199 °F
 ASTM D638
6.5 %
<br>@Temperature 150 °C
 6.5 %
<br>@Temperature 302 °F
 ASTM D638
Tensile Modulus 4.38 GPa
<br>@Temperature 150 °C
 635 ksi
<br>@Temperature 302 °F
 ASTM D638
7.59 GPa
<br>@Temperature 93.0 °C
 1100 ksi
<br>@Temperature 199 °F
 ASTM D638
10.7 GPa
<br>@Temperature 23.0 °C
 1550 ksi
<br>@Temperature 73.4 °F
 ASTM D638
10.7 GPa
<br>@Temperature 23.0 °C
 1550 ksi
<br>@Temperature 73.4 °F
 ISO 527
11.2 GPa
<br>@Temperature -40.0 °C
 1620 ksi
<br>@Temperature -40.0 °F
 ASTM D638
Flexural Strength 82.3 MPa
<br>@Temperature 150 °C
 11900 psi
<br>@Temperature 302 °F
 ASTM D790
98.6 MPa
<br>@Temperature 93.0 °C
 14300 psi
<br>@Temperature 199 °F
 ASTM D790
240 MPa
<br>@Temperature 23.0 °C
 34800 psi
<br>@Temperature 73.4 °F
 ASTM D790
276 MPa
<br>@Temperature -40.0 °C
 40000 psi
<br>@Temperature -40.0 °F
 ASTM D790
Flexural Modulus 2.80 GPa
<br>@Temperature 150 °C
 406 ksi
<br>@Temperature 302 °F
 ASTM D790
3.99 GPa
<br>@Temperature 93.0 °C
 579 ksi
<br>@Temperature 199 °F
 ASTM D790
8.96 GPa
<br>@Temperature 23.0 °C
 1300 ksi
<br>@Temperature 73.4 °F
 ASTM D790
9.66 GPa
<br>@Temperature -40.0 °C
 1400 ksi
<br>@Temperature -40.0 °F
 ASTM D790
Compressive Strength 241 MPa
<br>@Temperature 23.0 °C
 35000 psi
<br>@Temperature 73.4 °F
 ASTM D695
Shear Strength 74.5 MPa
<br>@Temperature 23.0 °C
 10800 psi
<br>@Temperature 73.4 °F
 ASTM D732
Izod Impact, Notched 0.850 J/cm
<br>@Temperature -40.0 °C
 1.59 ft-lb/in
<br>@Temperature -40.0 °F
 ASTM D256
0.900 J/cm
<br>@Temperature 23.0 °C
 1.69 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 6.40 J/cm
<br>@Temperature -40.0 °C
 12.0 ft-lb/in
<br>@Temperature -40.0 °F
 ASTM D4812
6.95 J/cm
<br>@Temperature 23.0 °C
 13.0 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D4812
Charpy Impact Unnotched 7.00 J/cm²
<br>@Temperature 23.0 °C
 33.3 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C
<br>@Temperature -40.0 - 23.0 °C
 278 µin/in-°F
<br>@Temperature -40.0 - 73.4 °F
 ASTM E 228
500 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 278 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ASTM E 228
500 µm/m-°C
<br>@Temperature 55.0 - 160 °C
 278 µin/in-°F
<br>@Temperature 131 - 320 °F
 ASTM E 228
CTE, linear, Transverse to Flow 56.0 µm/m-°C
<br>@Temperature -40.0 - 23.0 °C
 31.1 µin/in-°F
<br>@Temperature -40.0 - 73.4 °F
 ASTM E 228
60.0 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 33.3 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
60.0 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 33.3 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ASTM E 228
90.0 µm/m-°C
<br>@Temperature 55.0 - 160 °C
 50.0 µin/in-°F
<br>@Temperature 131 - 320 °F
 ASTM E 228
Deflection Temperature at 0.46 MPa (66 psi) 251 °C
484 °F
ASTM D648
251 °C
484 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 233 °C
451 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
<br>@Temperature 23.0 °C
 1.00e+15 ohm-cm
<br>@Temperature 73.4 °F
 ASTM D257
1.00e+17 ohm-cm
<br>@Temperature 23.0 °C
 1.00e+17 ohm-cm
<br>@Temperature 73.4 °F
 IEC 60093
Surface Resistance 1.00e+13 ohm
<br>@Temperature 23.0 °C
 1.00e+13 ohm
<br>@Temperature 73.4 °F
 ASTM D257
1.00e+13 ohm
<br>@Temperature 23.0 °C
 1.00e+13 ohm
<br>@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 4.1
<br>@Frequency 1.00e+6 Hz,<br> Temperature 23.0 °C
 4.1
<br>@Frequency 1.00e+6 Hz,<br> Temperature 73.4 °F
 ASTM D150
4.2
<br>@Frequency 1000 Hz,<br> Temperature 23.0 °C
 4.2
<br>@Frequency 1000 Hz,<br> Temperature 73.4 °F
 ASTM D150
Dielectric Strength 15.0 kV/mm
<br>@Thickness 3.20 mm,<br> Temperature 200 °C
 381 kV/in
<br>@Thickness 0.126 in,<br> Temperature 392 °F
 Short Time; ASTM D149
19.0 kV/mm
<br>@Thickness 3.20 mm,<br> Temperature 150 °C
 483 kV/in
<br>@Thickness 0.126 in,<br> Temperature 302 °F
 Short Time; ASTM D149
19.0 kV/mm
<br>@Thickness 3.20 mm,<br> Temperature 95.0 °C
 483 kV/in
<br>@Thickness 0.126 in,<br> Temperature 203 °F
 Short Time; ASTM D149
21.5 kV/mm
<br>@Thickness 1.57 mm,<br> Temperature 200 °C
 546 kV/in
<br>@Thickness 0.0618 in,<br> Temperature 392 °F
 Short Time; ASTM D149
21.5 kV/mm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 546 kV/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 Short Time; ASTM D149
23.0 kV/mm
<br>@Thickness 1.57 mm,<br> Temperature 95.0 °C
 584 kV/in
<br>@Thickness 0.0618 in,<br> Temperature 203 °F
 Short Time; ASTM D149
23.5 kV/mm
<br>@Thickness 1.57 mm,<br> Temperature 150 °C
 597 kV/in
<br>@Thickness 0.0618 in,<br> Temperature 302 °F
 Short Time; ASTM D149
25.0 kV/mm
<br>@Thickness 1.57 mm,<br> Temperature 23.0 °C
 635 kV/in
<br>@Thickness 0.0618 in,<br> Temperature 73.4 °F
 Short Time; ASTM D149
Dissipation Factor 0.0040
<br>@Frequency 1000 Hz,<br> Temperature 23.0 °C
 0.0040
<br>@Frequency 1000 Hz,<br> Temperature 73.4 °F
 ASTM D150
0.014
<br>@Frequency 1.00e+6 Hz,<br> Temperature 23.0 °C
 0.014
<br>@Frequency 1.00e+6 Hz,<br> Temperature 73.4 °F
 ASTM D150
Comparative Tracking Index 200 V
<br>@Thickness 3.00 mm,<br> Temperature 23.0 °C
 200 V
<br>@Thickness 0.118 in,<br> Temperature 73.4 °F
 UL 746A