DuPont Performance Polymers VTR 8525 (GBLT-S) GFLT-600 Formulation (discontinued **)
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8525 (GBLT-S) GFLT-600 Formulation
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationViton® GFLT 600
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 61 @Temperature 121 °C |
61 @Temperature 250 °F |
ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 17.2 MPa | 2490 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 172 % | 172 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000840 GPa | 0.122 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00710 GPa | 1.03 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 30 % @Temperature 200 °C |
30 % @Temperature 392 °F |
Method B, O-rings 22 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -24.2 °C | -11.6 °F | TR-10, 100% Elongation |
| Glass Transition Temp, Tg | -24.3 °C | -11.7 °F | DSC |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 2542 Non-Conductive Extruded Elastomer Specifications
- SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® LUX2414G PC (Asia Pacific)
- Industrial Laminates/Norplex NP310E Cotton Fabric
- Loxim 200 00V0 Polybutylene Terephthalate
- A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
- Aremco Corr-Paint™ CP4010S High Temperature Protective Coating Silicone-Polyester
Copyright © lookpolymers.com All Rights Reserved