DuPont Performance Polymers Zytel® HTN 51G35HSL NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 51G35HSL NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
35% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G35HSL NC010 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
50%RH; ISO 527-1/-2
220 MPa
31900 psi
DAM; ISO 527-1/-2
Tensile Stress 23.98 MPa

@Strain 0.560 %,
Temperature 150 °C
 3478 psi

@Strain 0.560 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
25.28 MPa

@Strain 0.240 %,
Temperature 23.0 °C
 3667 psi

@Strain 0.240 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
26.47 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 3839 psi

@Strain 0.230 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
26.51 MPa

@Strain 0.230 %,
Temperature 0.000 °C
 3845 psi

@Strain 0.230 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
26.73 MPa

@Strain 0.240 %,
Temperature 40.0 °C
 3877 psi

@Strain 0.240 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
27.02 MPa

@Strain 0.230 %,
Temperature -20.0 °C
 3919 psi

@Strain 0.230 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
28.85 MPa

@Strain 0.250 %,
Temperature 0.000 °C
 4184 psi

@Strain 0.250 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
29.4 MPa

@Strain 0.240 %,
Temperature -20.0 °C
 4260 psi

@Strain 0.240 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
29.81 MPa

@Strain 0.260 %,
Temperature 40.0 °C
 4324 psi

@Strain 0.260 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
31.35 MPa

@Strain 0.280 %,
Temperature 90.0 °C
 4547 psi

@Strain 0.280 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
33.7 MPa

@Strain 0.360 %,
Temperature 90.0 °C
 4890 psi

@Strain 0.360 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
34.48 MPa

@Strain 0.730 %,
Temperature 150 °C
 5001 psi

@Strain 0.730 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
51.14 MPa

@Strain 2.21 %,
Temperature 150 °C
 7417 psi

@Strain 2.21 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
59.63 MPa

@Strain 3.87 %,
Temperature 150 °C
 8649 psi

@Strain 3.87 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
62.2 MPa

@Strain 5.52 %,
Temperature 150 °C
 9020 psi

@Strain 5.52 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
63.98 MPa

@Strain 2.90 %,
Temperature 150 °C
 9280 psi

@Strain 2.90 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
69.22 MPa

@Strain 7.21 %,
Temperature 150 °C
 10040 psi

@Strain 7.21 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
70.63 MPa

@Strain 5.04 %,
Temperature 150 °C
 10240 psi

@Strain 5.04 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
95.73 MPa

@Strain 1.41 %,
Temperature 90.0 °C
 13880 psi

@Strain 1.41 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
103.1 MPa

@Strain 0.920 %,
Temperature 40.0 °C
 14950 psi

@Strain 0.920 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
103.49 MPa

@Strain 0.890 %,
Temperature 0.000 °C
 15010 psi

@Strain 0.890 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
105.15 MPa

@Strain 0.930 %,
Temperature 23.0 °C
 15251 psi

@Strain 0.930 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
105.24 MPa

@Strain 0.880 %,
Temperature -20.0 °C
 15264 psi

@Strain 0.880 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
105.24 MPa

@Strain 0.930 %,
Temperature 23.0 °C
 15264 psi

@Strain 0.930 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
110.26 MPa

@Strain 1.01 %,
Temperature 40.0 °C
 15992 psi

@Strain 1.01 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
111.11 MPa

@Strain 1.12 %,
Temperature 90.0 °C
 16115 psi

@Strain 1.12 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
112.6 MPa

@Strain 0.970 %,
Temperature 0.000 °C
 16330 psi

@Strain 0.970 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
112.85 MPa

@Strain 2.46 %,
Temperature 90.0 °C
 16368 psi

@Strain 2.46 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
114.7 MPa

@Strain 3.51 %,
Temperature 90.0 °C
 16640 psi

@Strain 3.51 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
115.46 MPa

@Strain 0.970 %,
Temperature -20.0 °C
 16746 psi

@Strain 0.970 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
153.83 MPa

@Strain 1.97 %,
Temperature 90.0 °C
 22311 psi

@Strain 1.97 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
163.9 MPa

@Strain 1.61 %,
Temperature 40.0 °C
 23770 psi

@Strain 1.61 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
165.58 MPa

@Strain 1.61 %,
Temperature 23.0 °C
 24015 psi

@Strain 1.61 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
166.29 MPa

@Strain 1.54 %,
Temperature 0.000 °C
 24118 psi

@Strain 1.54 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
166.4 MPa

@Strain 1.76 %,
Temperature 40.0 °C
 24130 psi

@Strain 1.76 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
167.14 MPa

@Strain 1.62 %,
Temperature 23.0 °C
 24242 psi

@Strain 1.62 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
169.5 MPa

@Strain 2.80 %,
Temperature 90.0 °C
 24580 psi

@Strain 2.80 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
172.39 MPa

@Strain 1.54 %,
Temperature -20.0 °C
 25003 psi

@Strain 1.54 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
180.66 MPa

@Strain 1.69 %,
Temperature 0.000 °C
 26203 psi

@Strain 1.69 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
186.98 MPa

@Strain 1.69 %,
Temperature -20.0 °C
 27119 psi

@Strain 1.69 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
196.3 MPa

@Strain 2.50 %,
Temperature 40.0 °C
 28470 psi

@Strain 2.50 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
204.62 MPa

@Strain 2.31 %,
Temperature 40.0 °C
 29678 psi

@Strain 2.31 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
208.09 MPa

@Strain 2.31 %,
Temperature 23.0 °C
 30181 psi

@Strain 2.31 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
213.2 MPa

@Strain 2.20 %,
Temperature 0.000 °C
 30920 psi

@Strain 2.20 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
214.3 MPa

@Strain 2.30 %,
Temperature 23.0 °C
 31080 psi

@Strain 2.30 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
224.8 MPa

@Strain 2.20 %,
Temperature -20.0 °C
 32600 psi

@Strain 2.20 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
226.6 MPa

@Strain 2.40 %,
Temperature 0.000 °C
 32870 psi

@Strain 2.40 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
239.35 MPa

@Strain 2.40 %,
Temperature -20.0 °C
 34715 psi

@Strain 2.40 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
Elongation at Break 2.2 %
2.2 %
50%RH; ISO 527-1/-2
2.4 %
2.4 %
DAM; ISO 527-1/-2
Tensile Modulus 12.0 GPa
1740 ksi
DAM; ISO 527-1/-2
12.0 GPa
1740 ksi
50%RH; ISO 527-1/-2
Flexural Modulus 10.5 GPa
1520 ksi
DAM; ISO 178
10.5 GPa
1520 ksi
50%RH; ISO 178
Shear Modulus 0.993 GPa

@Temperature 150 °C
 144 ksi

@Temperature 302 °F
 DAM; Dynamic; ISO 11403-1 -2
2.3613 GPa

@Temperature 110 °C
 342.48 ksi

@Temperature 230 °F
 DAM; Dynamic; ISO 11403-1 -2
2.48 GPa

@Temperature 60.0 °C
 360 ksi

@Temperature 140 °F
 DAM; Dynamic; ISO 11403-1 -2
2.6424 GPa

@Temperature 10.0 °C
 383.25 ksi

@Temperature 50.0 °F
 DAM; Dynamic; ISO 11403-1 -2
2.7253 GPa

@Temperature -20.0 °C
 395.28 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
2.91 GPa

@Temperature -50.0 °C
 422 ksi

@Temperature -58.0 °F
 DAM; Dynamic; ISO 11403-1 -2