DuPont Performance Polymers Zytel® HTN 92G45DH2 BK083 Polyphthalamide (PPA)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 92G45DH2 BK083 Polyphthalamide (PPA).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
35% Glass Reinforced PPA High Performance Polyamide with DuPont Zytel HTN92G45DH2 BK083 is a 45% glass reinforced high performance polyamide resin using DuPont SHIELD Technology with high flow and excellent retention of properties after aging at elevatInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 168 MPa
24400 psi
50%RH; ISO 527-1/-2
214 MPa
31000 psi
DAM; ISO 527-1/-2
Tensile Stress 3.94 MPa

@Strain 0.0400 %,
Temperature 180 °C
 571 psi

@Strain 0.0400 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
4.52 MPa

@Strain 0.0500 %,
Temperature 150 °C
 656 psi

@Strain 0.0500 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
4.78 MPa

@Strain 0.0500 %,
Temperature 0.000 °C
 693 psi

@Strain 0.0500 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
5.34 MPa

@Strain 0.0400 %,
Temperature 90.0 °C
 775 psi

@Strain 0.0400 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
6.13 MPa

@Strain 0.0400 %,
Temperature 23.0 °C
 889 psi

@Strain 0.0400 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
7.13 MPa

@Strain 0.0500 %,
Temperature 40.0 °C
 1030 psi

@Strain 0.0500 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
12.26 MPa

@Strain 0.190 %,
Temperature 180 °C
 1778 psi

@Strain 0.190 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
13.69 MPa

@Strain 0.190 %,
Temperature 150 °C
 1986 psi

@Strain 0.190 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
15.77 MPa

@Strain 0.160 %,
Temperature 90.0 °C
 2287 psi

@Strain 0.160 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
19.8 MPa

@Strain 0.140 %,
Temperature 23.0 °C
 2870 psi

@Strain 0.140 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
22.33 MPa

@Strain 0.150 %,
Temperature 40.0 °C
 3239 psi

@Strain 0.150 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
22.45 MPa

@Strain 0.170 %,
Temperature 0.000 °C
 3256 psi

@Strain 0.170 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
27.33 MPa

@Strain 0.300 %,
Temperature 90.0 °C
 3964 psi

@Strain 0.300 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
29.77 MPa

@Strain 0.220 %,
Temperature 0.000 °C
 4318 psi

@Strain 0.220 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
32.99 MPa

@Strain 0.590 %,
Temperature 180 °C
 4785 psi

@Strain 0.590 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
33.22 MPa

@Strain 0.230 %,
Temperature 23.0 °C
 4818 psi

@Strain 0.230 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
33.34 MPa

@Strain 0.520 %,
Temperature 150 °C
 4836 psi

@Strain 0.520 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
34.71 MPa

@Strain 0.250 %,
Temperature 40.0 °C
 5034 psi

@Strain 0.250 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
47.72 MPa

@Strain 0.560 %,
Temperature 90.0 °C
 6921 psi

@Strain 0.560 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
48.89 MPa

@Strain 1.07 %,
Temperature 180 °C
 7091 psi

@Strain 1.07 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
49.63 MPa

@Strain 0.350 %,
Temperature 0.000 °C
 7198 psi

@Strain 0.350 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
50.0 MPa

@Strain 0.900 %,
Temperature 150 °C
 7250 psi

@Strain 0.900 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
63.23 MPa

@Strain 0.460 %,
Temperature 40.0 °C
 9171 psi

@Strain 0.460 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
73.66 MPa

@Strain 0.520 %,
Temperature 23.0 °C
 10680 psi

@Strain 0.520 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
77.82 MPa

@Strain 3.20 %,
Temperature 180 °C
 11290 psi

@Strain 3.20 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
84.05 MPa

@Strain 4.84 %,
Temperature 180 °C
 12190 psi

@Strain 4.84 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
89.32 MPa

@Strain 2.97 %,
Temperature 150 °C
 12950 psi

@Strain 2.97 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
96.98 MPa

@Strain 4.74 %,
Temperature 150 °C
 14070 psi

@Strain 4.74 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
112.3 MPa

@Strain 2.00 %,
Temperature 90.0 °C
 16290 psi

@Strain 2.00 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
131.75 MPa

@Strain 3.39 %,
Temperature 90.0 °C
 19109 psi

@Strain 3.39 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
156.79 MPa

@Strain 1.32 %,
Temperature 40.0 °C
 22741 psi

@Strain 1.32 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
173.51 MPa

@Strain 1.39 %,
Temperature 23.0 °C
 25166 psi

@Strain 1.39 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
176.09 MPa

@Strain 1.34 %,
Temperature 0.000 °C
 25540 psi

@Strain 1.34 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
198.25 MPa

@Strain 2.06 %,
Temperature 40.0 °C
 28754 psi

@Strain 2.06 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
218.51 MPa

@Strain 2.10 %,
Temperature 23.0 °C
 31692 psi

@Strain 2.10 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
237.87 MPa

@Strain 2.20 %,
Temperature 0.000 °C
 34500 psi

@Strain 2.20 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 2.2 %
2.2 %
DAM; ISO 527-1/-2
2.5 %
2.5 %
50%RH; ISO 527-1/-2
Tensile Modulus 12.5 GPa
1810 ksi
50%RH; ISO 527-1/-2
15.0 GPa
2180 ksi
DAM; ISO 527-1/-2
Flexural Strength 300 MPa
43500 psi
DAM; ISO 178
Flexural Modulus 13.0 GPa
1890 ksi
DAM; ISO 178
Secant Modulus 1.71 GPa

@Strain 4.13 %,
Temperature 200 °C
 248 ksi

@Strain 4.13 %,
Temperature 392 °F
 DAM; ISO 11403-1 -2
2.26 GPa

@Strain 2.82 %,
Temperature 200 °C
 327 ksi

@Strain 2.82 %,
Temperature 392 °F
 DAM; ISO 11403-1 -2
3.04 GPa

@Strain 1.74 %,
Temperature 200 °C
 441 ksi

@Strain 1.74 %,
Temperature 392 °F
 DAM; ISO 11403-1 -2
4.12 GPa

@Strain 0.910 %,
Temperature 200 °C
 598 ksi

@Strain 0.910 %,
Temperature 392 °F
 DAM; ISO 11403-1 -2
5.605 GPa

@Strain 0.200 %,
Temperature 200 °C
 812.9 ksi

@Strain 0.200 %,
Temperature 392 °F
 DAM; ISO 11403-1 -2
7.10 GPa

@Strain 0.0500 %,
Temperature 200 °C
 1030 ksi

@Strain 0.0500 %,
Temperature 392 °F
 DAM; ISO 11403-1 -2
9.56 GPa

@Strain 0.0500 %,
Temperature 0.000 °C
 1390 ksi

@Strain 0.0500 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
11.5 GPa

@Strain 1.45 %,
Temperature 40.0 °C
 1660 ksi

@Strain 1.45 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
12.1 GPa

@Strain 1.52 %,
Temperature 23.0 °C
 1750 ksi

@Strain 1.52 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
12.7 GPa

@Strain 1.49 %,
Temperature 0.000 °C
 1850 ksi

@Strain 1.49 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
12.9 GPa

@Strain 0.980 %,
Temperature 40.0 °C
 1870 ksi

@Strain 0.980 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
13.2 GPa

@Strain 0.170 %,
Temperature 0.000 °C
 1920 ksi

@Strain 0.170 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
13.4 GPa

@Strain 1.05 %,
Temperature 23.0 °C
 1950 ksi

@Strain 1.05 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
13.4 GPa

@Strain 0.240 %,
Temperature 0.000 °C
 1950 ksi

@Strain 0.240 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
13.7 GPa

@Strain 0.610 %,
Temperature 40.0 °C
 1980 ksi

@Strain 0.610 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
13.9 GPa

@Strain 0.330 %,
Temperature 40.0 °C
 2010 ksi

@Strain 0.330 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
14.0 GPa

@Strain 0.950 %,
Temperature 0.000 °C
 2030 ksi

@Strain 0.950 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
14.1 GPa

@Strain 0.680 %,
Temperature 23.0 °C
 2050 ksi

@Strain 0.680 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2