Eastman E6838-796F Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman E6838-796F Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
E6838-796F is a low density formulation with no slip or antiblock. It is suggested for film applications requiring a good balance of properties, such as converter film for industrial packaging, general-purpose packaging, and disposable diaper film. As supplied by Eastman, E6838-796F may lawfully be used in food-contact applications under the FDA regulations at 21 CFR177.1520 (c)(2.2). Users must make their own determination that their use of this product is safe, legal, and technically suitable for their intended applications.Unless otherwise noted, all tests are run at 23°C and 50% RH. Extrusion conditions used to produce blown film: 1.9:1 blow-up ratio.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D4883
Moisture Vapor Transmission 18.6 cc-mm/m²-24hr-atm
47.2 cc-mil/100 in²-24hr-atm
ASTM F372
Oxygen Transmission 200 cc-mm/m²-24hr-atm
508 cc-mil/100 in²-24hr-atm
ASTM D1434
Thickness 38.0 microns
1.50 mil
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 250 %
250 %
ASTM D882
Film Elongation at Break, TD 750 %
750 %
ASTM D882
Secant Modulus, MD 0.186 GPa
27.0 ksi
1% Secant; ASTM D882
Secant Modulus, TD 0.220 GPa
31.9 ksi
1% Secant; ASTM D882
Coefficient of Friction >= 2.0
>= 2.0
ASTM D1894
Elmendorf Tear Strength MD 400 g
400 g
Elmendorf Tear Strength TD 140 g
140 g
Elmendorf Tear Strength, MD 10.5 g/micron
267 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.70 g/micron
94.0 g/mil
ASTM D1922
Dart Drop 2.60 g/micron
66.0 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 26.0 MPa
3770 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 94.0 °C
201 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 70 %
70 %
at 45°; ASTM D2457
Transmission, Visible 95 %
95 %
ASTM D1746
Descriptive Properties Value Comments
Process Film