ExxonMobil Escorene® LD-740 High EVA Film and Compounding Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD-740 High EVA Film and Compounding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer resin for specialty film and compounding applications. Outstanding heat sealability along with excellent strength properties are key attributes of films made from LD-740.Applications: Heat seal layer in coextruded and laminated structures; Compounding.

Physical Properties	Metric	English	Comments
Density	0.948 g/cc	0.0342 lb/in³	Exxon Method
Environmental Stress Crack Resistance	>= 500 hour	>= 500 hour	F50, Condition A; ASTM D1693
Melt Flow	5.5 g/10 min	5.5 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	81	81	ASTM D2240
Hardness, Shore D	31	31	ASTM D2240
Tensile Strength, Ultimate	17.0 MPa	2470 psi	ASTM D638
Tensile Strength, Yield	3.40 MPa	493 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0310 GPa	4.50 ksi	1% Secant, ASTM D790
Tensile Impact Strength	600 kJ/m²	286 ft-lb/in²	23°C; ASTM D-1822

Thermal Properties	Metric	English	Comments
Melting Point	77.0 °C	171 °F	Exxon Method
Vicat Softening Point	52.0 °C	126 °F	1000g; ASTM D-1525
Brittleness Temperature	<= -76.0 °C	<= -105 °F	ASTM D746