- Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film
Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film
| Category | Polymer , Film , Thermoplastic , Nylon |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 1200Matte is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock. 1200Matte film has a matte appearance on one side. The matte surface provides superior scuff resistance while maintaining excellent contact clarity. Applications: thermal lamination films used in book cover applications.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Thickness | 14.0 microns | 0.550 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 65 - 100 % | 65 - 100 % | ASTM D882 |
| Film Elongation at Break, TD | 65 - 100 % | 65 - 100 % | ASTM D882 |
| Secant Modulus, MD | 2.59 - 3.45 GPa | 376 - 500 ksi | ASTM D882 |
| Secant Modulus, TD | 2.59 - 3.45 GPa | 376 - 500 ksi | ASTM D882 |
| Coefficient of Friction | 0.40 - 0.50 | 0.40 - 0.50 | film to stainless steel; ASTM D1894 |
| 0.50 - 0.60 | 0.50 - 0.60 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1300 | 1100 - 1300 | graves tear, grams/mil (initial); ASTM D1004 |
| Film Tensile Strength at Break, MD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.0 - 2.0 % | 1.0 - 2.0 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.00 - 0.50 % | 0.00 - 0.50 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 6.5 - 8.5 % | 6.5 - 8.5 % | at 20° |
Users viewing this material also viewed the following:
- Gharda Chemicals GATONE™ 5400 PEEK, Medium Viscosity Grade (discontinued **)
- Reltek BONDiT™ A-53 Bonding Agent, Adhesive and Primer
- Kolon KOCETAL® K300BK Black Colored Grade Acetal Resin
- LG Chemical LUMID LW4303B(W) PA66+MF30%, Low Warpage
- Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating
- DSM Novamid® 1015GH35 BK37 PA6-GF35
- ChevronTexaco Multifak® EP NLGI Grade 0
- 3M Scotchcal™ 50-1 Graphic Film
- 3M 4200 Marine Adhesive/Sealant Fast Cure
Copyright © lookpolymers.com All Rights Reserved