IBC Advanced Alloys Beralcast® 310 Beryllium-Aluminum Alloy
| Category | Metal , Metal Matrix Composite , Nonferrous Metal , Beryllium Alloy |
| Manufacturer | IBC Advanced Alloys |
| Trade Name | Beralcast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IBC Advanced Alloys Beralcast® 310 Beryllium-Aluminum Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This alloy, a metal matrix composite, consisting of between 60 and 70% Be (by weight) is a wrought product offered by IBC Engineered Materials to be used in the process of manufacturing extrusions for a broad spectrum of industries. BeAl-310 is used primarily for select directional, higher strength applications.Information provided by IBC Advanced Alloys
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.16 g/cc | 0.0780 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 426.1 MPa | 61800 psi | |
| Tensile Strength, Yield | 325.4 MPa | 47200 psi | |
| Elongation at Break | 13.2 % | 13.2 % | Longitudinal |
| Modulus of Elasticity | 202 GPa | 29300 ksi | in tension |
| Compressive Yield Strength | 318.5 MPa | 46190 psi | |
| Bearing Yield Strength | 566.1 MPa | 82110 psi | Pin Type (e/D = 2.0) |
| Fatigue Strength | 220.6 MPa @# of Cycles 1.00e+7 |
32000 psi @# of Cycles 1.00e+7 |
Axial (R = -1.0) |
| Shear Strength | 299.9 MPa | 43500 psi | Pin Double Shear Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 °C |
7.33 µin/in-°F @Temperature 77.0 °F |
Longitudinal |
| Specific Heat Capacity | 1.423 J/g-°C | 0.3402 BTU/lb-°F | |
| Thermal Conductivity | 180 W/m-K | 1250 BTU-in/hr-ft²-°F | Longitudinal |
| Melting Point | 585 °C | 1090 °F | |
| Liquidus | 585 °C | 1090 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 26.6 - 38.5 % | 26.6 - 38.5 % | |
| Beryllium, Be | 60 - 70 % | 60 - 70 % | |
| Cobalt, Co | <= 0.20 % | <= 0.20 % | |
| Germanium, Ge | <= 0.20 % | <= 0.20 % | |
| Iron, Fe | <= 0.20 % | <= 0.20 % | |
| Silicon, Si | <= 0.25 % | <= 0.25 % | |
| Silver, Ag | 1.5 - 2.5 % | 1.5 - 2.5 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000410 ohm-cm | 0.00000410 ohm-cm |
Users viewing this material also viewed the following:
- MV Labs Y870 Y2(C2O4)3·9H2O Yttrium oxalate hydrate
- PolyOne Edgetek® X AS/018 White Acrylonitrile Butadiene Styrene (ABS)
- Lehmann & Voss LUVOTECH® GS 46 Polyamide 46, lubricant modified, heat stabilized
- Minelco UltraCarb LH15C-10 Hydrated Magnesium Calcium Carbonate
- DuPont Teijin Films Mylar® MO21 Polyester Film, 1000 Gauge
- Dow Corning 43 Paperaid
- Aclo Accutech Nylon 6 NY0730G30L Glass Reinforced
- BASF Lupranate® M20HB Isocyanate
- CENTROPLAST CENTROLEN PP GF 30 Polypropylene 30% glass fiber
Copyright © lookpolymers.com All Rights Reserved