IRPC Polimaxx Polene 1111NX TA4 Polypropylene Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Polene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IRPC Polimaxx Polene 1111NX TA4 Polypropylene Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER WITH 20% TALCUM REINFORCEDAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 36.3 MPa | 5260 psi | ASTM D638 |
| Elongation at Break | 11 % | 11 % | ASTM D638 |
| Flexural Yield Strength | 53.4 MPa | 7750 psi | ASTM D790 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Temperature 23.0 °C |
0.551 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 1200 A Zip 22 Natural Polyamide 66 (Nylon 66)
- Ineos R01C-01 Polypropylene Random Copolymer
- Sylvin Technologies 8925-90 Natural PVC Extrusion Compound
- Techmer ES HiFill® PA11 GB30 HS 30% Glass Bead Filled
- Saint-Gobain Norton® Fluorglas® Chemfilm® R191 Skived Sintered PTFE Tape (0.003" thick)
- Epoxyset Epoxibond EB-130M-1 Unfilled Epoxy Adhesive
- Aremco Corr-Paint™ CP4040 High Temperature Protective Coating Silicone
- Polykemi AB POLYabs H00 ABS, Heat Resistant
- Lucent Polymers TPP-220 Polypropylene, 20% Talc Filled, Impact Modified
Copyright © lookpolymers.com All Rights Reserved