Industrial Laminates/Norplex NP511 Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP511 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Woven glass fabric with high temperature epoxy resin. Excellent mechanical strength and electrical properties at elevated temperatures. Continuous operating temperature is 165°C. Material meets or exceeds NEMA G-11 standard and has been produced using the same materials as listed in the NIST G11CR specification for materials used in cryogenic applications, but not to the exact same quantities of ingredients as specified in the process specification.Thickness Tested: 0.062", 0.125" & 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.80 - 1.90 g/cc

@Thickness 1.57 mm
 1.80 - 1.90 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.20 %

@Thickness 1.57 mm
 0.20 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100 - 120

@Thickness 1.57 mm
 100 - 120

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 255 MPa

@Thickness 1.57 mm
 37000 psi

@Thickness 0.0620 in
 CW; ASTM D638
296 MPa

@Thickness 1.57 mm
 43000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 18.6 GPa

@Thickness 1.57 mm
 2700 ksi

@Thickness 0.0620 in
 CW; ASTM D229
20.7 GPa

@Thickness 1.57 mm
 3000 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 483 MPa

@Thickness 1.57 mm
 70000 psi

@Thickness 0.0620 in
 CW; ASTM D790
552 MPa

@Thickness 1.57 mm
 80000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 434 MPa

@Thickness 12.7 mm
 63000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 152 MPa

@Thickness 15.7 mm
 22000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 4.81 J/cm

@Thickness 12.7 mm
 9.00 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
6.41 J/cm

@Thickness 12.7 mm
 12.0 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 15.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.33 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 185 °C
365 °F
Glass Transition Temp, Tg 165 °C
329 °F
Tg
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 4.38

@Thickness 1.57 mm
 4.38

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 31.5 kV/mm

@Thickness 1.57 mm
 800 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
35.4 kV/mm

@Thickness 1.57 mm
 900 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 55000 V

@Thickness 1.57 mm
 55000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
60000 V

@Thickness 1.57 mm
 60000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.020

@Thickness 1.57 mm
 0.020

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 120 sec

@Thickness 3.17 mm
 120 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 150 V

@Thickness 3.17 mm
 150 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 2200 lb
0.5", ASTM D229
Color Natural