Loxim 810 02T HB Polypropylene Compound, 10% Talc Filled, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler , Polypropylene, Flame Retardant
Manufacturer Loxim Industries
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Loxim 810 02T HB Polypropylene Compound, 10% Talc Filled, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Loxim Industries
Physical Properties Metric English Comments
Specific Gravity 0.920 - 1.02 g/cc
0.920 - 1.02 g/cc
ASTM D792
Filler Content 10 %
10 %
Linear Mold Shrinkage 0.015 - 0.017 cm/cm
0.015 - 0.017 in/in
ASTM D1299
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 - 37.0 MPa
5080 - 5370 psi
ASTM D683
Flexural Modulus 1.70 - 1.90 GPa
247 - 276 ksi
ASTM D790
Izod Impact, Notched 0.400 - 0.450 J/cm
0.749 - 0.843 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 100 - 105 °C
212 - 221 °F
ASTM D1525, HDT Method B
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in