NOVA Chemicals Novapol® TF-0242-E Hexene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® TF-0242-E Hexene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent stiffness and glossApplications: Diaper back sheet, BlendingFilm properties are typical of film extruded at 270°C.Information provided by NOVA Chemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 1000 % | 1000 % | ASTM D882 |
| Secant Modulus, MD | 0.385 GPa | 55.8 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.450 GPa | 65.3 ksi | at 1%; ASTM D882 |
| Impact | 70 | 70 | J/mm; NOVA Chemicals Puncture test |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 12.0 g/micron | 305 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 87 % | 87 % | at 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC T25020 Polypropylene Copolymer, Mineral Reinforced
- SABIC Innovative Plastics Lexan® IR2840 PC (Europe-Africa-Middle East)
- Momentive Performance Materials RTV6424 Heat-Curing Silicone Adhesive, White
- Teknor Apex Telcar® TL-2635D Thermoplastic Elastomer
- A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene
- Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 63%/120 E-Glass Fiber
- DSM Stanyl® TS241B3 PA46-CF15
- Axiall 11800 Wire & Cable Flexible PVC
- Formosa Plastics Formolene® L64220U Rotational Molding LLDPE (discontinued **)
- Ineos Nova 6110 Super High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved