PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T6

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T6.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
High stiffness and elongation at rupture. Property data for Condition T6 (Quench in water at RT).Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.679 - 2.961 g/cc
0.09679 - 0.1070 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 144
>= 144
Tensile Strength >= 123 MPa
<br>@Temperature 300 °C
 >= 17800 psi
<br>@Temperature 572 °F
>= 338 MPa
<br>@Temperature 200 °C
 >= 49000 psi
<br>@Temperature 392 °F
>= 491 MPa
<br>@Temperature 20.0 °C
 >= 71200 psi
<br>@Temperature 68.0 °F
Tensile Strength, Yield >= 122 MPa
<br>@Temperature 300 °C
 >= 17700 psi
<br>@Temperature 572 °F
>= 318 MPa
<br>@Temperature 200 °C
 >= 46100 psi
<br>@Temperature 392 °F
>= 429 MPa
<br>@Temperature 20.0 °C
 >= 62200 psi
<br>@Temperature 68.0 °F
Elongation at Break >= 9.3 %
<br>@Temperature 20.0 °C
 >= 9.3 %
<br>@Temperature 68.0 °F
>= 14.4 %
<br>@Temperature 200 °C
 >= 14.4 %
<br>@Temperature 392 °F
>= 21.2 %
<br>@Temperature 300 °C
 >= 21.2 %
<br>@Temperature 572 °F
Modulus of Elasticity >= 58.0 GPa
<br>@Temperature 300 °C
 >= 8410 ksi
<br>@Temperature 572 °F
>= 65.0 GPa
<br>@Temperature 200 °C
 >= 9430 ksi
<br>@Temperature 392 °F
>= 72.0 GPa
<br>@Temperature 20.0 °C
 >= 10400 ksi
<br>@Temperature 68.0 °F
Poissons Ratio 0.341
<br>@Temperature 20.0 °C
 0.341
<br>@Temperature 68.0 °F
0.347
<br>@Temperature 100 °C
 0.347
<br>@Temperature 212 °F
0.354
<br>@Temperature 150 °C
 0.354
<br>@Temperature 302 °F
0.361
<br>@Temperature 200 °C
 0.361
<br>@Temperature 392 °F
0.364
<br>@Temperature 250 °C
 0.364
<br>@Temperature 482 °F
0.369
<br>@Temperature 300 °C
 0.369
<br>@Temperature 572 °F
Shear Modulus 23.0 GPa
<br>@Temperature 300 °C
 3340 ksi
<br>@Temperature 572 °F
24.0 GPa
<br>@Temperature 200 °C
 3480 ksi
<br>@Temperature 392 °F
24.0 GPa
<br>@Temperature 250 °C
 3480 ksi
<br>@Temperature 482 °F
25.0 GPa
<br>@Temperature 150 °C
 3630 ksi
<br>@Temperature 302 °F
26.0 GPa
<br>@Temperature 100 °C
 3770 ksi
<br>@Temperature 212 °F
28.0 GPa
<br>@Temperature 20.0 °C
 4060 ksi
<br>@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 22.9 - 23.9 µm/m-°C
<br>@Temperature 20.0 - 100 °C
 12.7 - 13.3 µin/in-°F
<br>@Temperature 68.0 - 212 °F
23.7 - 24.7 µm/m-°C
<br>@Temperature 20.0 - 200 °C
 13.2 - 13.7 µin/in-°F
<br>@Temperature 68.0 - 392 °F
24.5 - 25.5 µm/m-°C
<br>@Temperature 20.0 - 300 °C
 13.6 - 14.2 µin/in-°F
<br>@Temperature 68.0 - 572 °F
Thermal Conductivity 121.9 W/m-K
<br>@Temperature 30.0 °C
 846.0 BTU-in/hr-ft²-°F
<br>@Temperature 86.0 °F
130.9 W/m-K
<br>@Temperature 100 °C
 908.4 BTU-in/hr-ft²-°F
<br>@Temperature 212 °F
144.6 W/m-K
<br>@Temperature 200 °C
 1004 BTU-in/hr-ft²-°F
<br>@Temperature 392 °F
155.7 W/m-K
<br>@Temperature 300 °C
 1081 BTU-in/hr-ft²-°F
<br>@Temperature 572 °F
156.1 W/m-K
<br>@Temperature 400 °C
 1083 BTU-in/hr-ft²-°F
<br>@Temperature 752 °F
Melting Point 512 - 659 °C
954 - 1220 °F
Solidus 512.3 - 518.3 °C
954.1 - 964.9 °F
Liquidus 653.6 - 659.3 °C
1208 - 1219 °F
Component Elements Properties Metric English Comments
Aluminum, Al 94 %
94 %
As Balance
Copper, Cu 5.0 %
5.0 %
Titanium, Ti 1.0 %
1.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000570 - 0.00000610 ohm-cm
0.00000570 - 0.00000610 ohm-cm