- PolyOne Geon™ Vinyl Rigid Extrusion 87771 Polyvinyl Chloride, Rigid (PVC, Rigid)
PolyOne Geon™ Vinyl Rigid Extrusion 87771 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87771 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.72 GPa | 395 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 80.6 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.74 GPa | 397 ksi | ASTM D790 |
| Izod Impact, Notched | 2.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
4.12 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 6.80 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
12.7 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| 12.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
22.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 64.9 J/cm @Temperature 23.0 °C |
0.122 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 159 J/cm @Temperature 23.0 °C |
0.298 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C | 37.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.7 °C @Thickness 3.18 mm |
161 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | AAMA 303 | |
| Ease of Sizing | Excellent | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| Profile Extrusion | ||
| PVC Cell Classification | 1-41434-33 | ASTM D4216 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Outdoor Applications | |
| Profiles | ||
| Windows & Doors |
Users viewing this material also viewed the following:
- Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate
- Solvay Specialty Polymers Catalyst CT/2-HP Polyolefin
- Styrolution Polystyrol 158 K GR 21 PS
- Samsung Cheil Industries Starex® SR-0330M ABS, Unreinforced Heat Resistant
- Styron CALIBREâ„¢ 5201 15 Polycarbonate, 20% Glass Reinforced
- A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- CMW® ELKONITE® 10W3 Copper Tungsten RWMA Class 11
- Huntsman PE1076 Film Extrusion Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved