Polyram RamShine PV701 ABS, UV Stabilized
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Polyram RamShine PV701 ABS, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV stabilized ABS for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | DIN 53479 |
| Water Absorption | 0.30 % | 0.30 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Melt Flow | 22 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C |
22 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM-D638 |
| Elongation at Break | 35 % | 35 % | ASTM-D638 |
| Tensile Modulus | 2.15 GPa | 312 ksi | ASTM-D790 |
| Flexural Strength | 65.0 MPa | 9430 psi | ASTM-D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
| Izod Impact, Notched | 3.00 J/cm <br>@Temperature 23.0 °C |
5.62 ft-lb/in <br>@Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | DIN 53461 |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM-D1525 |
| Flammability, UL94 | HB <br>@Thickness 3.00 mm |
HB <br>@Thickness 0.118 in |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CR350CL Polypropylene, Random Copolymer, Clarified, Lubricated
- ExxonMobil Escorene® LX-0252 LMDPE Rotational Molding Grade (discontinued **)
- Inno-Comp INNOPOL® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer
- Taiwan PU Corporation TPUI-E98 General Grade, Injection Molding Polyester Base TPU
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
- Westlake LF2040 Hexene Linear Low Density Polyethylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 15 Minutes Milling
- ExxonMobil LD 071.LQ Blown Film Resin
- ConocoPhillips Sulnap® 22 Cutting Oil
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/8hr/AC
Copyright © lookpolymers.com All Rights Reserved