- SABIC Innovative Plastics LNP Lubricomp TX03476 PU
SABIC Innovative Plastics LNP Lubricomp TX03476 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp TX03476 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| 0.86 % @Time 86400 sec |
0.86 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | Type I, 5 mm/min; ASTM D 638 |
| 7.00 MPa | 1020 psi | 5 mm/min; ISO 527 | |
| Elongation at Yield | 177.4 % | 177.4 % | Type I, 5 mm/min; ASTM D 638 |
| 316.9 % | 316.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 0.0400 GPa | 5.80 ksi | 50 mm/min; ASTM D 638 |
| 0.0400 GPa | 5.80 ksi | 1 mm/min; ISO 527 | |
| Impact Test | 54.0 J | 39.8 ft-lb | Multiaxial Impact; ISO 6603 |
| 41.0 J @Temperature 23.0 °C |
30.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 267 °C @Thickness 3.20 mm |
513 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Lucent Polymers ABS-305LG Acrylonitrile Butadiene Styrene, General Purpose, Low Gloss
- Solvay Specialty Polymers Galden® SV135 PFPE Solvent
- Saint-Gobain CHR® 2302-3R UHMW Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Zotefoams Evazote® EV30 Ethylene Vinyl Acetate Copolymer Foam
- Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- Teknor Apex APEX® 04-A0386B-88 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved