SABIC Innovative Plastics LNP THERMOCOMP UX08325 PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UX08325 PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UX08325 is PPA base glass fiber filled compounds, good for LDS (Laser direct structuring)application. Additional feature is high heat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.530 % | 0.530 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0041 cm/cm | 0.0041 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0052 cm/cm | 0.0052 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| 2.0 % | 2.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 10.88 GPa | 1578 ksi | 50 mm/min; ASTM D638 |
| 11.08 GPa | 1607 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 194 MPa | 28100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 194 MPa | 28100 psi | 2 mm/min; ISO 178 |
| 197 MPa | 28600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.61 GPa | 1390 ksi | 2 mm/min; ISO 178 |
| 9.77 GPa | 1420 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.51 J/cm | 6.58 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.2 @Frequency 1.00e+9 Hz |
4.2 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.010 @Frequency 1.00e+9 Hz |
0.010 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Renegade Materials Corporation MVK-14 Polyimide FreeForm™ S2-Glass Fabric
- SABIC Innovative Plastics Lexan® FXE1414T PC Copolymer (Europe-Africa-Middle East)
- Lubriplate 630-AA Lithium Based Multi-Purpose Grease
- Guarniflon SC 1400 Polytetrafluoroethylene Seal
- Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes
- Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Conditioned
- Shin-Etsu Silicones 562P Fluid
- TIMCAL TIMREX® C-LUB 306 Primary Synthetic Graphite
- Westlake EF421 Low Density Polyethylene
- Lucobit Lucofin® 1412-t1 Polyolefin TPO Granules, Light Grey
Copyright © lookpolymers.com All Rights Reserved