SABIC Innovative Plastics LNP Thermotuf WF006I Polyester, TP
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermotuf WF006I Polyester, TP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* WF006I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.474 g/cc | 0.05325 lb/in³ | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm @Time 86400 sec |
0.0029 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0129 cm/cm @Time 86400 sec |
0.0129 in/in @Time 24.0 hour |
ISO 294 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D 638 |
| Tensile Strength, Yield | 107 MPa | 15500 psi | ASTM D 638 |
| 109 MPa | 15800 psi | ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 |
| 3.9 % | 3.9 % | ASTM D 638 | |
| Elongation at Yield | 2.1 % | 2.1 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D 638 | |
| Tensile Modulus | 6.52 GPa | 946 ksi | 1 mm/min; ISO 527 |
| 8.96 GPa | 1300 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 173 MPa | 25100 psi | ASTM D 790 |
| 181 MPa | 26300 psi | ISO 178 | |
| Flexural Modulus | 7.51 GPa | 1090 ksi | ASTM D 790 |
| 8.62 GPa | 1250 ksi | ISO 178 | |
| Izod Impact, Notched | 1.86 J/cm @Temperature 23.0 °C |
3.48 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 9.98 J/cm @Temperature 23.0 °C |
18.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² @Temperature 23.0 °C |
30.5 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® D 3000 AE Expandable Polystyrene (discontinued **)
- PolyOne Geon™ Vinyl Flexible C70UB Polyvinyl Chloride, Flexible (PVC, Flexible)
- Hexion UP 802 Unsaturated Polyester Resin, High Surface Quality, Low Shrinkage, High Arc Resistance
- Shakespeare NX-806 Saltwater Nylon Copolymer Fishing Line, 30 lb
- SABIC Innovative Plastics LNP THERMOCOMP MFB71L PP (Asia Pacific)
- Zircar Refractory Composites RSBL-SOL6 Silica-Magnesia Blanket
- ExxonMobil Enable™ 23-05HH Metallocene Polyethylene Resin
- Fainplast Compounds GK 72/R Flexible PVC, Flame Retardant Sheathing Lead Free
- BASF Elastollan 1185 A W TPUR
- 3M 4108 Foam Tape
Copyright © lookpolymers.com All Rights Reserved