Solvay Specialty Polymers Torlon® 4645 Polyamide-imide (PAI)
| Category | Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Torlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Torlon® 4645 Polyamide-imide (PAI).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Torlon® 4645, an injection-moldable, wear-resistant grade of polyamide-imide (PAI), has been formulated to give outstanding wear resistance in lubricated wear applications.Features: Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Wear Resistance; High Heat Resistance; High Stiffness; High Temperature Strength; Low Friction; Self Lubricating; Semi ConductiveUses: Automotive Applications; Bearings; Bobbins; Bushings; Seals; Thrust WasherAdditional Properties: Coefficient of Linear Thermal Expansion - ASTM D696 1.4E-5 cm/cm/°C; Wear Factor - ASTM D3702 1.60 in³·min^-10/ft·lb·hr; Wear Factor - ASTM D3702 0.300 in³·min^-10/ft·lb·hrInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 |
| Tensile Modulus | 18.6 GPa | 2700 ksi | ASTM D638 |
| Flexural Strength | 154 MPa | 22300 psi | ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ASTM D790 |
| Compressive Strength | 157 MPa | 22800 psi | ASTM D695 |
| Shear Strength | 60.7 MPa @Temperature 150 °C |
8800 psi @Temperature 302 °F |
ASTM D732 |
| 85.5 MPa @Temperature 23.0 °C |
12400 psi @Temperature 73.4 °F |
ASTM D732 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.070 - 0.090 | 0.070 - 0.090 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 281 °C | 538 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 °C | 579 °F | |
| Nozzle Temperature | 371 °C | 700 °F | |
| Mold Temperature | 199 - 216 °C | 390 - 421 °F | |
| Drying Temperature | 177 °C @Time 10800 sec |
351 °F @Time 3.00 hour |
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Back Pressure | 6.89 MPa | 999 psi | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Carbon Fiber + PTFE Lubricant | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Form | Pellets | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw L/D Ratio | 18.0:1.0 to 24.0:1.0 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 713-40 Reactive Alumina
- Ovation Polymers OPTRENE 10GF Polypropylene, 10% Glass Reinforced
- Petroquimica Triunfo Tritheva® TN 2020 EVA Copolymer
- Fine Organics FINALUX G 711 Lubricant Additive
- SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Asia Pacific)
- Tipco Tipcolite® TMS 111 Phenolic Compound, Cellulose Pulp, in fluffy form, having Soft Flow & High Strength
- Eurotec® Tecolen® HP10 GR20 NL PPCP, 20% glass fiber reinforced, natural
- DuPont Elvax® 210 Ethylene Vinyl Acetate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved