Spartech PP5110 Talc Filled Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech PP5110 Talc Filled Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc @Temperature 22.8 °C |
0.960 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Filler Content | 10 % | 10 % | |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125inch wall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 1.59 GPa | 230 ksi | secant; ASTM D790 |
| 2.07 GPa | 300 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 0.347 J/cm @Temperature 22.8 °C |
0.650 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 2.71 J @Temperature 22.8 °C |
2.00 ft-lb @Temperature 73.0 °F |
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 60 % | 60 % | 60°; ASTM D523 |
Users viewing this material also viewed the following:
- Rogers Corporation RO4533 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate
- Cytec EN-9 (Conap) Casting, Potting, and Molding Compound
- C.O.I.M. EXTER S® S 104 L Orthophthalic Resin
- A. Schulman ComAlloy Hiloy® 283 PPO Alloy, Glass Reinforced
- Carpenter HyMu "80"® Electronic Alloy, Bar, After Process Anneal
- DSM Akulon® K224-PG8 Impact Modified Nylon 6-40% Glass Reinforced (European Grade) (Dry)
- LG Chemical HF350U ABS, High Flow
- Arkema Group Pebax® MX 1205 SP 01 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved