Techmer ES HiFill® PA6 0232 B Barium Sulfate Filler
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6 0232 B Barium Sulfate Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Barium SulfateFeatures: High Specific GravityInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.32 g/cc | 0.0838 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.5 MPa | 6600 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Strength | 49.0 MPa | 7100 psi | ASTM D790 |
| Flexural Modulus | 6.34 GPa | 920 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 167 °C | 333 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 - 1.00e+14 ohm-cm | 1.00e+13 - 1.00e+14 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Parker Chomerics C-Wing™ Heat Spreader
- Parker Chomerics Tecknit NC-Consil® FR751 Nickel Coated Graphite Filled Silicone Elastomer
- Kazanorgsintez 153-10K Polyethylene Composition for Cable Industry
- Ineos Nova T163B Expandable Polystyrene
- Dow Corning SYL-OFF® PMCP7362 Coating
- CP-Polymer-Technik Wellamid® 6000/58 HWUVCP Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry
- Dow SiLK™ I300 560 Semiconductor Dielectric Resin
- Arlon 56609R028 0.029" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M FV092R Soft Translucent Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved