Techmer ES Luriblend® PS 06001
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PS 06001.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler/Unspecified FillerReinfor.Information provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.600 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C | 33.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 100 ohm-cm | 10 - 100 ohm-cm | ASTM D257 |
| Surface Resistance | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Outokumpu 4742 High Temperature Ferritic Stainless Steel
- Kolon SPESIN® KP2122G15VO G/F Reinforced & Retardant PBT Resin (discontinued **)
- H.C. Starck WCu 75/25 Tungsten-Copper Composite Material
- LATI Latilub 75/4-20T PBT, PTFE Filled
- Shuman 780H Grey ABS
- Tisan TISESTER® Flame Retardant (V0). Heat Stabilized Polybutylene Terephthalate
- American Elements Boron Nitride Nanoparticles
- EMS-Grivory Grivory® HT2V-3X V0 nat 6059 PA6T/66-GF30
- Bhansali Engineering Abstron KU650NH ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved