Unitika FUN-8000
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Unitika FUN-8000.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: High impact strength High chemical resistance Transparency as high as polycarbonateInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % <br>@Thickness 3.17 mm,<br> Time 86400 sec |
0.15 % <br>@Thickness 0.125 in,<br> Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm <br>@Thickness 3.00 mm |
0.0080 in/in <br>@Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 78 % | 78 % | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 4.50 J/cm <br>@Thickness 3.17 mm |
8.43 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 87 % <br>@Thickness 3.00 mm |
87 % <br>@Thickness 0.118 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | |
| Middle Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | actual surface temp |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 8.00 - 24.0 hour | 8.00 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG38F ABS
- SABIC Innovative Plastics Lexan® HFD1830 PC Copolymer (Asia Pacific)
- PolyOne OnColor™ 30BKA488 Black Polyvinyl Chloride, Unspecified (PVC, Unspecified)
- Custom Resins Duratel™ MF27 Acetal Copolymer (discontinued **)
- Saint-Gobain Versilicâ„¢ SPX-70I.B. High Strength Silicone Pressure Tubing Formulation
- Chosun Refractories HSC-18RA Dense and High-Strength Castable, Superdense
- DuPont Teijin Films Mylar® D804 Polyester Film, 60 Gauge
- LNP Lubricomp® QFL-4036 BK8-115 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant (disconti
- Solvay RHODASURF® T 50 Surfactant
- SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved