- Total PPR 8573 Polypropylene, Film Extrusion Grade
Total PPR 8573 Polypropylene, Film Extrusion Grade
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | PPR |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPR 8573 Polypropylene, Film Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Random copolymer heat sealable film gradeColor/Clarity/Impact - FINA 8573 is a low melting, high ethylene random copolymer with improved color, optics and impact properties.Heat Sealable - The low melting point of FINA 8573 makes it a very good heat seal layer for oriented films.Slip/Antiblock - FINA 8573 is available with custom slip and antiblock packages.FDA - FINA 8573 complies with FDA regulations Title 21 CFR Section 177.1520(c) 3.1 and may be used under these provisions for food contact and applications.Recommended Applications - FINA 8573 is recommended for use in non- oriented cast film processes for manufacture of packaging films that require improved optical and impact properties and as a heat seal layer for oriented films.Processing - FINA 8573 resin processes on film extrusion equipment with typical melt temperatures of 390- 450°F (199-232°C).Data provided by the manufacturer, Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Permeability | 14.0 g mil/ (m2 day) @Temperature 37.8 °C |
0.903 g mil/ (100 in2 day) @Temperature 100 °F |
90% RH; ASTM E96 |
| Density | 0.895 g/cc | 0.0323 lb/in³ | ASTM D1505 |
| Melt Flow | 6.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 500 % | 500 % | Non-oriented film; ASTM D882 |
| Secant Modulus | 0.483 GPa | 70.1 ksi | 1% Secant Modulus; Non-oriented Film; ASTM D882 |
| Dart Drop | 9.40 g/micron | 239 g/mil | F<sub>50</sub>; ASTM D 1709 |
| Seal Strength | >= 200 g/25 mm | >= 200 g/in | at 135°C, 15 psi pressure and 1 sec. |
| Film Tensile Strength at Break, MD | 21.0 MPa | 3050 psi | Non-oriented film; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 135 °C | 275 °F | DSC |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | Non-oriented film; ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; Non-oriented film; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | film extrusion |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IS7015X X-Ply Cross-Ply Polypropylene-Glass Composite
- Orion Engineered Carbons PUREX® HS 22 Carbon Black
- Kraton® D1161 K (SIS) Linear Triblock Copolymer
- SABIC Innovative Plastics LNP Lubricomp YP003 TPEE
- SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific)
- SABIC Innovative Plastics LNP VERTON MV00AS PP (Europe-Africa-Middle East)
- TIMCAL TIMREX® MX25 Primary Synthetic Graphite
- BASF Styropor® BFL 327 EPS
- Aptek DI-STRATE 95210 Microwave/RF Foam Substrate
- DuPont Performance Polymers Hytrel® 4068 TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved