Toyobo GLAMIDE® TY-592GHV 6T-Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-592GHV 6T-Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-592GHV is a flame resistant, aromatic 6T-Nylon. It is of halogen origin and contains 55% GF.55
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.81 g/cc | 1.81 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 55 % | 55 % | |
| Water Absorption | 0.10 % | 0.10 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0030 - 0.0060 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0060 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 90.0 MPa @Temperature 80.0 °C |
13100 psi @Temperature 176 °F |
Practical Use (Water Absorption 0.8%); ASTM-D638 |
| 170 MPa @Temperature 80.0 °C |
24700 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D638 | |
| 245 MPa @Temperature 23.0 °C |
35500 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 280 MPa @Temperature -40.0 °C |
40600 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D638 | |
| 295 MPa @Temperature -40.0 °C |
42800 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 1.8 % | 1.8 % | Absolute Drying; ASTM-D638 |
| Flexural Strength | 125 MPa @Temperature 80.0 °C |
18100 psi @Temperature 176 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 |
| 230 MPa @Temperature 80.0 °C |
33400 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 310 MPa @Temperature 23.0 °C |
45000 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 330 MPa @Temperature 23.0 °C |
47900 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 380 MPa @Temperature -40.0 °C |
55100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 400 MPa @Temperature -40.0 °C |
58000 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 8.10 GPa @Temperature 80.0 °C |
1170 ksi @Temperature 176 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 |
| 15.0 GPa @Temperature 80.0 °C |
2180 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 17.0 GPa @Temperature 23.0 °C |
2470 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 17.5 GPa @Temperature 23.0 °C |
2540 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 18.0 GPa @Temperature -40.0 °C |
2610 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D790 | |
| 19.0 GPa @Temperature -40.0 °C |
2760 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 1.40 J/cm @Temperature -40.0 °C |
2.62 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 1.40 J/cm @Temperature -40.0 °C |
2.62 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 0.8%); ASTM-D256 | |
| 1.50 J/cm @Temperature 23.0 °C |
2.81 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.80 J/cm @Temperature 23.0 °C |
3.37 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 0.8%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C | 8.89 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 270 °C | >= 518 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 264 °C | 507 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM-D257 |
| Dielectric Constant | 4.3 @Frequency 1000 Hz |
4.3 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 0.8%); ASTM-D149 |
| 26.0 kV/mm @Thickness 2.00 mm |
660 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Arc Resistance | 25 sec | 25 sec | ASTM-D495 |
| Comparative Tracking Index | 350 V | 350 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | |
| Mold Temperature | 150 °C | 302 °F | |
| Injection Pressure | 135 MPa | 19600 psi |
Users viewing this material also viewed the following:
- MV Labs BE1000 BeSO4.4H2O Beryllium sulfate tetrahydrate
- RheTech Products FT1001-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 16% Plasticizer (discontinued **)
- H.C. Starck Grade A Silicon Hexaboride, SiB6
- Lehmann & Voss LUVOCOM® AC-80/TF/22/BK Polyacetal-copolymer, with PTFE
- 3M FP024408 Removable Clear Polypropylene Label Products
- Lubrizol ESTANE® 54630 Ether Based Thermoplastic Polyurethane (European Grade)
- DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, General Description (disc
Copyright © lookpolymers.com All Rights Reserved