- Polymer Property : Melt Flow = 4.0 g/10 min
Polymer Property : Melt Flow = 4.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 190 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 374 °F |
ISO 1133 |
| Premix Thermoplastics PRE-ELEC® TPE 1502 Conductive Thermoplastic Compound PRE-ELEC® TPE 1502 is a conductive thermoplastic compound based on a thermoplastic elastomer (TPE). Conductivity is achieved by using a special conductive carbon black. In addition to a low electri.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Noble Polymers Regis™ 275107 Thermoplastic Olefin (TPO) Regis is a TPO (thermoplastic olefin) produced by Noble Polymers based on olefin/elastomer compounding. We have created Regis for use in bumpers and bumper fascias, air dams, exterior panels, materi.. |
|||
| Melt Flow | 4.0 - 9.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
4.0 - 9.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP1 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 265F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Injection MoldingNotes: All physical, mechanical and thermal testing.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| SABIC M40060 Series High Density Polyethylene for Injection Molding Product Description: M40060 is a high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good rigid.. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Fiberfil® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced Information provided by FIBERFIL Engineered Plastics |
|||
| Melt Flow | 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Global ABS-704 General Purpose High Impact ABS Information provided by Global Polymers Corporation. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 5402 BLK The burn rate is 0.7 in/min based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D-1238 |
| Multibase Multi-Flex® TPE A 5904 LC BLK Multi-Flex® LC compounds are a new generation elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Shell's Kraton G technology and fe.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® A 9402 MR TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good .. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 12.5 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 27.6 lb, Temperature 446 °F |
ISO 1133 |
| Shanghai Ofluorine 9201F PVDF Powder for cables Description: Excellent mechanical properties, heat resistance and flame resistance, PVDF for cable can bear high temperature, corrosive chemicals etc harsh working environment, which has low smoke, .. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg |
4.0 g/10 min @Load 4.76 lb |
ISO 1133 |
| SIDPEC EGYPTENE® HD 3840 EA MDPE Wire and Cable Grade Applications:Suitable for the production of silane cross-linkable compoundsLow voltage power cable insulationInjection molded technical parts and closureInformation provided by Interchim s.r.l., off.. |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Styrolution Zylar 650 MBS Zylar® 650 is an impact modified styrene acrylic copolymer that provides a balance of clarity and toughness, with outstanding strength and rigidity. Zylar 650 also has superior processing charact.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Total PPH 4069 Polypropylene Homopolymer, Fiber Polypropylene PPH 4069 is a homopolymer polypropylene with a Melt Flow index of 4 g/10 min.Polypropylene PPH 4069 is intended for extrusion of high tenacity staple fibers for non-woven applications... |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133H |
| Total PS CPDS 9217 Compound Polystyrene/Polyethylene POLYSTYRENE (PS) COMPOUND (CPDS) 9217 is an alloy of polystyrene and polyethylene. This combination brings the benefits of polyethylene; a high level of stress crack resistance, mechanical properti.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 3491 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3491 is a low water carry over homopolymer polypropylene, designed for high speed extrusion.Information provided by A. Schulman. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High.. |
|||
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Cossa Polimeri ESTADIENE 0420 HHT Acrylonitrile Butadiene Styrene ABS for injection molding or extrusionVery high thermal resistance, good impact resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ELASTO UK Dryflex® 420351S SBS Based Material, 35D Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Diamond Polymers NPP30-0400 MGF30 30% Mineral & Glass Filled Homopolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg |
4.0 g/10 min @Load 4.76 lb |
|
| Dow HDPE 04452N High Density Polyethylene DOW HDPE 04452N resin is a narrow molecular weight distribution copolymer designed to offer good stress crack resistance and stacking strength with excellent impact strength. This resin has moderate.. |
|||
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Chi Mei Polyrex® PG-80 Polystyrene High strength |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Aclo Accutech Nylon 6 NY0730G20L Glass Reinforced |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Aclo Accutech Polyethylene HD0234G20UVL High Density Glass Reinforced UV Stabilized |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Braskem MR 435 UV LMDPE Rotational Molding Polyethylene Applications: Water tanks; toys; automotive components. Information provided by Braskem |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
|
| BASF Polystyrol® 585 K Impact Grade Polystyrene (Europe) Special high gloss, high-impact grade for all types of housings. Basis product for gloss capping.Data was collected by ISO methods and provided by BASF. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Asahi Kasei Thermylene® P7-40FG-0790 40% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Melt Flow | 4.0 g/10 min @Load 1.05 kg, Temperature 190 °C |
4.0 g/10 min @Load 2.31 lb, Temperature 374 °F |
ASTM D1238 |
| DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer
(Unverified Data**) Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con.. |
|||
| Melt Flow | 4.0 - 14 g/10 min @Load 12.5 kg, Temperature 232 °C |
4.0 - 14 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR FLEX® 2750-01 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |
|||