Physical Properties | Metric | English | Comments |
---|---|---|---|
Oxidative Stability | 125 hour @Temperature 316 °C, Pressure 1.03 MPa |
125 hour @Temperature 600 °F, Pressure 150 psi |
<1.5% wt loss |
Renegade Materials Corporation MVK-14 Polyimide FreeForm™ Astroquartz 4581 Fabric MVK-14 Polyimide Astroquartz and S2 glass prepregs are an affordable, easy-to-process material for high-temperature radome and antenna applications. MVK-14 is a non-MDA alternative to BMI, cyanate e.. |
|||
Oxidative Stability | 125 hour @Temperature 316 °C, Pressure 1.03 MPa |
125 hour @Temperature 600 °F, Pressure 150 psi |
<1.5% wt loss |
Renegade Materials Corporation MVK-14 Polyimide FreeForm™ S2-Glass Fabric MVK-14 Polyimide Astroquartz and S2 glass prepregs are an affordable, easy-to-process material for high-temperature radome and antenna applications. MVK-14 is a non-MDA alternative to BMI, cyanate e.. |
|||
Oxidative Stability | 125 hour @Temperature 316 °C, Pressure 1.03 MPa |
125 hour @Temperature 600 °F, Pressure 150 psi |
<2% wt loss |
Renegade Materials Corporation MVK-14 Polyimide FreeForm™ T650-35 8HS Carbon Fabric MVK-14 polyimide prepregs are a more affordable and easier-to-process, non-carcinogenic alternative to PMR-15 and other older polyimide chemistries. MVK-14 offers a more durable alternative to high-.. |