Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 62 µm | 62 µm | Average Diameter |
Potters Industries Conduct-O-Fil® SA270S30 Silver-coated Aluminum Granules Applications:EMI shielding in contact with aluminumConductive adhesivesAerospace and marine applicationsAdvantages:Low density with high conductivityLow galvanic corrosion in contact with aluminumIn.. |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 515.074 Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12 HS Number: 28499030 |
|||
Particle Size | 62 µm | 62 µm | minimum of 95% less than, Cr3C2 |
H.C. Starck Amperit® 585.3 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) Composition is of Cr3C2 only |
|||
Particle Size | 62 µm | 62 µm | minimum 99.5% |
H.C. Starck Amperit® 588.059 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 703.1 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 62 µm | 62 µm | 100% less than |
H.C. Starck Amperit® 704.053 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 62 µm | 62 µm | 100% less than |
H.C. Starck Amperit® 704.072 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 712.074 Chromium Oxide-Titanium Oxide 75-25 (Cr2O3-TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 716.054 Chromium Oxide-Titanium Oxide-Silicon Oxide 92-3-5 (Cr2O3-TiO2-SiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 90% less than |
H.C. Starck Amperit® 716.066 Chromium Oxide-Titanium Oxide-Silicon Oxide 92-3-5 (Cr2O3-TiO2-SiO2) |
|||
Particle Size | 62 µm | 62 µm | 100% less than |
H.C. Starck Amperit® 742.068 Aluminum Oxide-Titanium Oxide 97-3 (Al2O3-TiO2) |
|||
Particle Size | 62 µm | 62 µm | 100% less than |
H.C. Starck Amperit® 744 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 744.3 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 745.3 Aluminum Oxide-Titanium Oxide 60-40 (Al2O3-TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 782.3 Titanium Oxide (TiO2) |
|||
Particle Size | 62 µm | 62 µm | 100% less than |
H.C. Starck Amperit® 825 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 825.1 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 704.054 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 62 µm | 62 µm | Minimum of 90% less than |
H.C. Starck Amperit® 740.1 Aluminum Oxide (Al2O3) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 742.1 Aluminum Oxide-Titanium Oxide 97-3 (Al2O3-TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 744.1 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 745.1 Aluminum Oxide-Titanium Oxide 60-40 (Al2O3-TiO2) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 782.1 Titanium Oxide (TiO2) |
|||
Particle Size | 62 - 86 µm | 62 - 86 µm | d90, Guaranteed |
TIMCAL TIMREX® KS5-75TT Primary Synthetic Graphite TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all pro.. |
|||
Particle Size | 62 µm | 62 µm | TEC QSD |
Trelleborg AEM Eccospheres® SI-160 Sodium Borosilicate Glass Microspheres Eccospheres® glass microspheres are hollow thin-walled glass microspheres composed of sodium borosilicate glass. To the naked eye they resemble a fine, white, free-flowing powder. However, magnific.. |
|||
Particle Size | 62 µm | 62 µm | Average Diameter |
Potters Industries Conduct-O-Fil® SA270S20 Silver-coated Aluminum Granules Applications:EMI shielding in contact with aluminumConductive adhesivesAerospace and marine applicationsAdvantages:Low density with high conductivityLow galvanic corrosion in contact with aluminumIn.. |
|||
Particle Size | 62 µm | 62 µm | 99% less than |
H.C. Starck Amperit® 529.053 Tungsten Carbide - Hastalloy C 85-15 (NiMoCrFeCo) |
|||
Particle Size | 62 µm | 62 µm | Minimum of 95% less than |
H.C. Starck Amperit® 516.1 Tungsten Carbide - Cobalt (WC-Co) 88-12 HS Number: 28499030 |
|||
Particle Size | 62 µm | 62 µm | 100% less than |
H.C. Starck Amperit® 547.059 Tungsten Carbide-Nickel 88-12 (WC-Ni) |