Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.012 - 0.017 cm/cm | 0.012 - 0.017 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® PP 1394 Conductive Thermoplastic Compound PRE-ELEC® PP 1394 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Linear Mold Shrinkage | 0.0080 - 0.017 cm/cm | 0.0080 - 0.017 in/in | FRISETTA Test Method |
Nilit FRIANYL B63 H-KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.014 - 0.017 cm/cm | 0.014 - 0.017 in/in | as molded; ISO 294 |
Solvay Engineered Polymers DEXFLEX® 810HSF TPO
(discontinued **) Description: DEXFLEX® 810HSF is a thermoplastic olefinic elastomer (TPO) designed for large molded-in-color automotive exterior applications that require high flow characteristics for excellent pro.. |
|||
Linear Mold Shrinkage | 0.0090 - 0.017 cm/cm | 0.0090 - 0.017 in/in | FRISETTA Test Method |
Nilit FRIANYL A63 GV 5 Nylon 6.6 for injection molding, 5% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.0080 - 0.017 cm/cm | 0.0080 - 0.017 in/in | FRISETTA Test Method |
Nilit FRIANYL B63 W-SG30 Nylon 6 for injection molding, 30% mineral filled Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.010 - 0.017 cm/cm | 0.010 - 0.017 in/in | |
Lehmann & Voss LUVOCOM® 80-8510 Polyacetal-copolymer, with mineral filler, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Linear Mold Shrinkage | 0.014 - 0.017 cm/cm @Temperature 23.0 °C |
0.014 - 0.017 in/in @Temperature 73.4 °F |
ASTM D955 |
Kingfa PA66-C111 Toughened PA66 Features:High impactLow tendency to wrapExcellent balance propertiesApplications:Injection moldingSport applianceAutomobile partsPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Linear Mold Shrinkage | 0.0090 - 0.017 cm/cm | 0.0090 - 0.017 in/in | ISO 294-4:1997 |
Inno-Comp INNOPOL® CS 1-3810 10% Glass-Fiber-Filled Polypropylene Homopolymer INNOPOL® CS 1-3810 is a 10% glass-fiber-filled polypropylene homopolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 1-3810 is recommended for producing in.. |
|||
Linear Mold Shrinkage | 0.015 - 0.017 cm/cm | 0.015 - 0.017 in/in | ASTM D1299 |
Loxim 810 02T HB Polypropylene Compound, 10% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Linear Mold Shrinkage | 0.012 - 0.017 cm/cm | 0.012 - 0.017 in/in | |
Lehmann & Voss LUVOCOM® 1/TF/18/SI/2/BK Polyamide 66, with PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Linear Mold Shrinkage | 0.012 - 0.017 cm/cm | 0.012 - 0.017 in/in | ASTM D955 |
Kolon KOPA® KN133HR Heat Resistant Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Linear Mold Shrinkage | 0.013 - 0.017 cm/cm | 0.013 - 0.017 in/in | ASTM D955 |
Kolon KOPA® KN171 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Linear Mold Shrinkage | 0.013 - 0.017 cm/cm | 0.013 - 0.017 in/in | aged 48 hrs at 80; ISO 294 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Linear Mold Shrinkage | 0.013 - 0.017 cm/cm | 0.013 - 0.017 in/in | aged 48 hrs at 80; ISO 294 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Linear Mold Shrinkage | 0.012 - 0.017 cm/cm | 0.012 - 0.017 in/in | ASTM D955 |
Clariant 6602-L BK-02 Nylon 66, Lubricated, Nucleated, Weather Resistant, Black Data provided by Clariant Masterbatches |
|||
Linear Mold Shrinkage | 0.014 - 0.017 cm/cm | 0.014 - 0.017 in/in | after bake; ISO 294 |
Solvay Engineered Polymers DEXFLEX® 930HS TPO
(discontinued **) Description: DEXFLEX® 930HS is a thermoplastic olefinic elastomer (TPO) designed for large automotive exterior applications that require high flow for excellent processability, ductile impact prope.. |