Polymer Property : Linear Mold Shrinkage, Transverse = 0.0052 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in
Plastcom SLOVAMID 6/66 GF 30 FRG 5 TS PA6/66, 30% glass fibre, flame retardant FeaturesPA 6 + PA 66 alloy for injection moulding, chemically reinforced with 30 % glass fibre, with halogen and phosphorus free flame retardant. Main features: flammability in accordance with UL 94..
Linear Mold Shrinkage, Transverse	0.0052 - 0.0152 cm/cm @Thickness 3.17 mm	0.0052 - 0.0152 in/in @Thickness 0.125 in	ASTM D955
Network Polymers Softflex® 8103 Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP EX07305 PEI (Asia Pacific) Polyetherimide reinforced with Glass fiber and PTFE for use in Burn-in Test Sockets (BiTS) Application
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	ISO 294-4
Styron MAGNUMâ„¢ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin Overview: Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications Magnum 3325 SLG can achieve 60Â° Gardner gloss levels below 2.0 with low ..
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	SABIC Method
SABIC Innovative Plastics LNP STAT-KON 9X08403C Liquid Crystal Polymer (LCP) LNP* STAT-KON* 9X08403C is a compound based on Liquid Crystal Polymer (LCP) resin containing Carbon Fiber. Added features of this material are: Clean Compounding System, High Temperature, Flame Re..
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	GB/T 15585-1995
Sichuan Deyang HatonÂ® hMR61 Polyphenylene Sulfide, Glass & Mineral Reinforced Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	SABIC Method
SABIC Innovative Plastics LNP THERMOCOMP UX08325 PPA (Asia Pacific) LNP* Thermocomp* UX08325 is PPA base glass fiber filled compounds, good for LDS (Laser direct structuring)application. Additional feature is high heat.
Linear Mold Shrinkage, Transverse	0.0052 cm/cm	0.0052 in/in	ISO 294
BASF Ultrason S 2010 G4 20% Glass Filled PSU Ultrason S 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.