Polymer Property : Viscosity = 1.50e+6 cP Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F
DuPont Bynel® 3030 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin (discontinued **) Bynel® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F
DuPont Bynel® 3062 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin (discontinued **) Bynel® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F	estimated from log-log graph
DuPont Bynel® 4105 Anhydride-Modified LLDPE Adhesive Resin Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F	estimated from log-log graph
DuPont Bynel® 4125 Anhydride-Modified LLDPE Adhesive Resin Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F	estimated from log-log graph
DuPont Bynel® 4206 Anhydride-Modified LDPE Adhesive Resin Bynel® Series 4200 resins are anhydride-modified, low-density polyethylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process ..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F	estimated from log-log graph
DuPont Bynel® 50E571 Anhydride-Modified Polypropylene Adhesive Resin Bynel® Series 5000 resins are anhydride-modified polypropylene. Bynel® 50E561 and 50E571 are based on polypropylene random copolymers. They are available in pellet form for use in conventional ext..
Viscosity	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 240 °C	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 464 °F
DSM Akulon® F132 PA6 Film Extrusion, High Viscosity
Viscosity	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 240 °C	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 464 °F
DSM Akulon® F132-C1 PA6 Film Extrusion, High Viscosity, Lubricated
Viscosity	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 240 °C	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 464 °F
DSM Akulon® F132-E1 PA6 Medium/High Viscosity, Nucleated, Lubricated, Film Extrusion
Viscosity	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 240 °C	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 464 °F
DSM Akulon® F132-E2 PA6 High Viscosity, Nucleated, Lubricated, Film Extrusion
Viscosity	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 260 °C	1.50e+6 cP @Shear Rate 0.100 1/s, Temperature 500 °F
DSM Akulon® F234-C PA6 Film Extrusion, High Viscosity, Lubricated
Viscosity	1.50e+6 - 2.00e+6 cP @Shear Rate 100 1/s, Temperature 232 °C	1.50e+6 - 2.00e+6 cP @Shear Rate 100 1/s, Temperature 450 °F	Melt Viscosity; ASTM D3835
Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Viscosity	1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 232 °C	1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 450 °F	Melt Viscosity; ASTM D3835
Arkema Group KYNAR® 740 Black/Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistance; high purityAppli..
Viscosity	1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 232 °C	1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 450 °F	Melt Viscosity; ASTM D3835
Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Viscosity	1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 232 °C	1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 450 °F	Melt Viscosity; ASTM D3835
Arkema Group KYNAR® 741 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F	estimated from log-log graph
DuPont Bynel® 4107 Anhydride-Modified LLDPE Adhesive Resin (discontinued **) Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi..
Viscosity	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 190 °C	1.50e+6 cP @Shear Rate 50.0 1/s, Temperature 374 °F
DuPont Bynel® 41E557 Anhydride-Modified LLDPE Adhesive Resin (discontinued **) Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi..