Polymer Property : Melt Flow = 120 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	1.00 - 120 g/10 min	1.00 - 120 g/10 min	Average value: 7.88 g/10 min Grade Count:103
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values..
Melt Flow	1.50 - 120 g/10 min	1.50 - 120 g/10 min	Average value: 12.7 g/10 min Grade Count:74
Overview of materials for Polystyrene, Transparent Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Transparent Grade". Each property range of values reported is minimum and maximum values of..
Melt Flow	80 - 120 g/10 min	80 - 120 g/10 min	Melt Volume Rate (cmÂ³/10 min)
Huntsman IROGRANÂ® A 78 P 4766 TPU-Polyether Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman
Melt Flow	2.0 - 120 g/10 min @Load 5.00 kg, Temperature 190 °C	2.0 - 120 g/10 min @Load 11.0 lb, Temperature 374 °F	ASTM D1238
Aaron Industries AVPE LLD 300-2 Virgin Polyethylene Melt flow index may be specified.
Melt Flow	30.0 - 120 g/10 min	30.0 - 120 g/10 min	Average value: 63.3 g/10 min Grade Count:3
Overview of materials for PEKK, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate..
Melt Flow	1.00 - 120 g/10 min	1.00 - 120 g/10 min	Average value: 16.1 g/10 min Grade Count:403
Overview of materials for Polycarbonate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Molded". Each property range of values reported is minimum and maximum values of appropri..