Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® FL 23 Low Density Polyethylene - Blown Film Extrusion Riblene FL 23 is a low density polyethylene (LDPE) with added slip agent, suitable for blown film extrusion. Riblene FL 23 is characterized by a good balance between processability and mechanical p.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® FL 34 E Low Density Polyethylene - Blown Film Extrusion Riblene FL 34 E is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FL 34 E is characterized by a good balance between processab.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
DSM Yparex® 7102 Polyolefin Adhesive Resin (European Grade)
(discontinued **) The Yparex range provides outstanding adhesion for all forms of polyethylene including cross-linked PE to: barrier plastics like EVOH and Polyamidemetals like aluminum, steel and copper.Yparex offer.. |
|||
Melt Flow | 2.1 g/10 min | 2.1 g/10 min | ASTM D1238 |
ExxonMobil Escorene® LD 725.21 Molding, extrusion, compounding and adhesive resin
(discontinued **) Escorene Ultra LD 722.21 is 18 wt% vinyl acetate copolymer suitable for molding, extrusion, compounding and hot melt adhesive applications.Information provided by ExxonMobil Chemical |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
L; ASTM D1238 |
Global PP-2500-H Polypropylene Block Copolymer Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-crates, pallets, paint drum, storage & transport container, seatsInformation provided by Global Po.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
L; ASTM D1238 |
Global PP-2512-H Polypropylene Block Copolymer Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-special for wire & cable, telecom insulationInformation provided by Global Polymers Corporation. |
|||
Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.1 g/10 min @Load 11.0 lb, Temperature 392 °F |
old Condition G; ASTM D1238 |
Ineos Nova Styrosun® 6600 Weather Resistant High Impact Styrenic Polymer Features: Outdoor weatherablePhysical property retention after UV exposurePaintable and printableExcellent toughness Can be injection molded or co-extruded Easy to process, no drying required Appli.. |
|||
Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 280 °C |
2.1 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Appeel® LSR11D542 Lidding Sealant Resin Appeel® LSR11D542 is a modified ethylene vinyl acetate copolymer resin designed to function as a peelable sealing layer for lidding and pouch applications. It provides a peelable seal and a "whiten.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 30E671 Adhesive Resin Bynel® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p.. |
|||
Melt Flow | 2.1 g/10 min @Load 21.6 kg, Temperature 190 °C |
2.1 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133/G |
Total HDPE 56020 S High Density Polyethylene - Blow Molding HDPE 56020 S is a very high molecular weight (VHMW) high density polyethylene with a high resistance to impact, good chemical resistance and optimized balance between Environmental Stress Crack Resi.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Westlake EMAC® SP2255 17% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2255 is a 17% EMA copolymer containing slip and antiblock. This resin is designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat s.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total HDPE HD 6221 High Density Polyethylene - Blow Molding HDPE HD 6221 is a high density polyethylene with very high stiffness and impact resistance. The low viscosity of this grade has been designed for the manufacture of thin walled containers for foods.. |
|||
Melt Flow | 2.1 g/10 min @Temperature 230 °C |
2.1 g/10 min @Temperature 446 °F |
I<sub>2</sub>; ASTM D1238 |
Formosa Plastics Formolene® 5140H Compression Molding Polypropylene HomopolymerApplications: Compression Molded Caps and Closure ApplicationsFormolene 5140H DEVELOPMENTAL is a polypropylene homopolymer designed and formulated for compression molded caps and closure .. |
|||
Melt Flow | 2.1 g/10 min @Temperature 230 °C |
2.1 g/10 min @Temperature 446 °F |
I<sub>2</sub>; ASTM D1238 |
Formosa Plastics Formolene® 5143C Homopolymer Polypropylene Homopolymer for Extrusion Sheet and Thermoforming Applications Formolene® 5143C is a polypropylene homopolymer designed for sheet and thermoforming applications, which require exceptional clarity. .. |
|||
Melt Flow | 2.1 g/10 min @Temperature 230 °C |
2.1 g/10 min @Temperature 446 °F |
I<sub>2</sub>; ASTM D1238 |
Formosa Plastics Formolene® 5143H Homopolymer Polypropylene Hopolymer Formolene® 5143H is a polypropylene homopolymer designed for sheet and thermoforming applications requiring good clarity. It contains a unique combination of stabilizers, nucleators and a.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1133 |
DuPont™ Bynel® 30E753 Anhydride Modified Ethylene Vinyl Acetate BYNEL® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 124.MS Low Density Polyethylene Resin Product Description: LD 124.MS blown film resin offers an excellent balance of optical and strength properties for general purpose clear film applications. Availability: Latin America, North America.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
ExxonMobil PP1572 Polypropylene Homopolymer Product Description: A nucleated homopolymer resin designed for general-purpose compression molding of articles such as caps and closures. It exhibits excellent strength and high crystallization te.. |
|||
Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.1 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Diamond Polymers TR 5000 Description: Transparent ABSInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Dow AMPLIFY™ GR 207 Maleic anhydride grafted (MAH) polymer AMPLIFY™ GR 207 Functional Polymer is a maliec anhydride grafted (MAH) polymer. In tie layers for flexible packaging, it promotes adhesion of polyethylene to barrier polymers such as polyamide and.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow INSPIRE™ 117.00 Performance Polymer 117.00 Performance Polymer is a propylene-based resin intended for use in extrusion blow molding and thermoforming applications where stiffness, toughness, high temperature resistance, and clarity a.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® AESN G9 T6L Nylon 12, Graphite Filled (Conditioned) Designation ISO 1874-PA12,EHLS,22-010,CD10Rigid grade with graphite fillers for extrusion. Available color: steel gray. Reinforced light and heat stabilizing agents.Very low friction coefficient. No.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® AESN G9 T6L Nylon 12, Graphite Filled (Dry) Designation ISO 1874-PA12,EHLS,22-010,CD10Rigid grade with graphite fillers for extrusion. Available color: steel gray. Reinforced light and heat stabilizing agents.Very low friction coefficient. No.. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238L |
Braskem H 605 Thermoforming Polypropylene Applications: Flat and corrugated sheets with high transparency; thermoformed packing with high transparency. Information provided by Braskem |
|||
Melt Flow | 2.1 g/10 min | 2.1 g/10 min | Exxon Method |
ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 18% vinyl acetate copolymerApplications: Hot melt adhesives; Wax blends; Industrial sealants. |
|||
Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
NOVA Chemicals Novapol® LF-0218-AF LDPE Extrusion Resin
(discontinued **) Film Properties. Features: Good heat sealing latitude, moderate toughness, easy processability.Applications: Specifically designed for foam process, blends with LLDPE.Data provided by the manufactu.. |