Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 11.0 MPa | 1600 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1299 Conductive Thermoplastic Compound PRE-ELEC® PE 1299 is a conductive thermoplastic masterbatch/compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. PRE-ELEC® PE 1299 has a high concentration o.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | ASTM D2095 |
Permabond UV648 UV-curable Adhesive PERMABOND UV648 is a UV-curing adhesive developed for use on plastics. It has good adhesion to acrylic and contains a long-wavelength photo initiator to allow it to cure through UV-stabilized plasti.. |
|||
Tensile Strength | 11.0 MPa @Strain 100 % |
1600 psi @Strain 100 % |
Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV3805 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | Measured on a pressed sample; ISO 37 |
Kraton® D1170 B (SIBS) Linear Triblock Copolymer Description: Kraton D1165 P is a clear, linear triblock copolymer based on styrene and isoprene with a polystyrene content of 30%. It is supplied from North America in the physical form identified: .. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Addisilâ„¢ 1060 E Industrial Extrusion Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Addisilâ„¢ 2060 E Industrial Extrusion Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Siloprenâ„¢ CLS 5000 Liquid Silicone Rubber - Self-Bonding / Customized This LSR elastomer is a self-bonding, customized, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevate.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2645 Custom Liquid Silicone Rubber - Infant Care This LSR elastomer is a specialty grade, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated tempera.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Silplusâ„¢ 40 EX Heat Cured Rubber - Extrusion Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Silplusâ„¢ 40 HS High Strength Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Silplusâ„¢ 60 EX Heat Cured Rubber - Extrusion Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Silplusâ„¢ 60 MP Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Silplusâ„¢ 70 MP Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Lucite International Elvacite ® 2013 Acrylic Resin Elvacite® 2013 is a low molecular weight methyl methacrylate / n-butyl methacrylate copolymer. It is a fast – dissolving, low viscosity grade with quick solvent release for use in industrial.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Silplusâ„¢ 60 CW Heat Cured Rubber - Cable & Wire Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 - 15.0 MPa | 1600 - 2180 psi | Moulding Direction; BS2782:Pt3 |
Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue Applications & Industries: General: 25% Glass fibre is the most widely used filler. It improves the creep resistance, compressive strength, rigidity, and wear of PTFE, both at low & high temperature.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | ISO 527 |
Fainplast Compounds Hax™ HF 018/25 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Insulation; very low thicknessInformation provided by Fainplast Compounds |
|||
Tensile Strength | 11.0 MPa | 1600 psi | ASTM D412 |
Dynasol Solprene® 9320 Multi-branched Thermoplastic Rubber (Multi-branched SBS) Solprene® 9320 is a 68/32 Butadiene-Styrene multi arm copolymer, polymerized in solution process. It has a non-staining FDA approved antioxidant system for food contact applications and it is essen.. |
|||
Tensile Strength | 11.0 MPa @Strain 20.0 % |
1600 psi @Strain 20.0 % |
ISO 37 |
BASF Elastollan C 98 A TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
AlphaGary Garathane™ X 94-350-B UV-DG2 Polyurethane based compound 90°C rated flame retardant, polyether based, polyurethane compound |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
AlphaGary Megolon™ HF 8110 LD UV Low Smoke Halogen Free General purpose sheathing compound with good mechanical, processing properties and reduced die drool. UV resistant. Application examples include Data Cables, Optical Cables. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
AlphaGary Megolon™ S500 Low Smoke Halogen Free Sheathing compound allowing significantly improved processing speeds plus good mechanical properties. Application examples include Special Fire Survival / Power Low Voltage / Power Medium Voltage. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | ASTM D638 |
Aaron Industries AAROLENE® ARPE LD 300-1 LDPE Black Low Density Polyethylene AAROLENE® ARPE 300 Series Polyethylene Compounded Resin, LDPE BlackFeatures: A compounded LDPE, black, low melt resin specifically designed for all profile extrusion applications. |
|||
Tensile Strength | 11.0 MPa @Strain 300 % |
1600 psi @Strain 300 % |
ISO 37 |
BASF Elastollan C 85 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Momentive Performance Materials Addisil™ 2040 E Industrial Extrusion Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 11.0 MPa | 1600 psi | |
Teknor Apex Elexar® EL 1446A Thermoplastic Elastomer Notes: Elexar® is a family of styrene block copolymer thermoplastic elastomers, often referred to as thermoplastic rubber (TPR). Elexar® "rubber-like" compounds offer superior electrical properti.. |