Premix Thermoplastics PRE-ELEC® PE 1299 Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PE 1299 Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® PE 1299 is a conductive thermoplastic masterbatch/compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. PRE-ELEC® PE 1299 has a high concentration of carbon black and has been developed to be used as a masterbatch. PRE-ELEC® PE 1299 can be diluted up to 50% with natural or recycled HDPE. The actual amount should always be tested as it also depends on the processing parameters. PRE-ELEC® PE 1299 can be used both in injection moulding or extrusion of sheets, profiles, pipes etc.Processing: PRE-ELEC® PE 1299 compound can be processed in the injection moulding machines using normal processing conditions as with high density polyethylene.Test Specimen: 10[mm] wide moulded rod. The values below with the exception of MFI and specific gravity are measured from test bars moulded with 40% HDPE (MFI8).Information from Premix OY
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.025 - 0.035 cm/cm
0.025 - 0.035 in/in
ISO 294-4
Melt Flow 1.5 g/10 min

@Load 21.6 kg,
Temperature 190 °C
1.5 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 95
95
ISO 868
Hardness, Shore D 65
65
ISO 868
Tensile Strength 11.0 MPa
1600 psi
ISO 527
Tensile Strength, Yield 21.0 MPa
3050 psi
ISO 527
Elongation at Break 90 %
90 %
ISO 527
Elongation at Yield 12 %
12 %
ISO 527
Flexural Modulus 1.00 GPa
145 ksi
ISO 178
Izod Impact, Notched (ISO) 20.0 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
9.52 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature -20.0 °C
NB

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
Charpy Impact Unnotched NB

@Thickness 102 mm,
Temperature 23.0 °C
NB

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
NB

@Thickness 102 mm,
Temperature -20.0 °C
NB

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
Charpy Impact, Notched 1.70 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
8.09 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
5.50 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
26.2 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 65.0 °C
149 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 43.0 °C
109 °F
75/Method Af
Vicat Softening Point 58.0 °C
136 °F
ISO 306/B50
123 °C
253 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm
<= 1000 ohm-cm
ISO D-257
Surface Resistance <= 1e+05
<= 1e+05
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 200 °C
392 °F
Cylinder
240 °C
464 °F
Die
Zone 2 210 °C
410 °F
Cylinder
230 °C
446 °F
Die
Zone 3 220 °C
428 °F
Die
220 °C
428 °F
Cylinder
Zone 4 220 °C
428 °F
Cylinder
230 °C
446 °F
Die
Zone 5 230 °C
446 °F
Cylinder
240 °C
464 °F
Die
Melt Temperature 180 - 280 °C
356 - 536 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Roll Temperature 50.0 °C
122 °F
3rd Roll
60.0 °C
140 °F
2nd Roll
70.0 °C
158 °F
1st Roll
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate