Mechanical Properties | Metric | English | Comments |
---|---|---|---|
100% Modulus | 0.00630 GPa | 0.914 ksi | 12.5% change after 72 hours @ 200°C; ASTM D412 |
Precision Polymer Engineering Perlast® G80X Perfluoroelastomer A black perfluoroelastomer compound with excellent steam resistance and mechanical properties. It has extremely low outgassing properties.Applications: For use in applications which require exposure.. |
|||
100% Modulus | 0.00630 GPa | 0.914 ksi | |
Freudenberg Simrit Superiorâ„¢ F850 Fluoroelastomer Cost-effective, high performance compound for semiconductor applications. Superior F850 offers outstanding plasma resistance and low particulation in a wide range of plasma environments. |
|||
100% Modulus | 0.00630 GPa | 0.914 ksi | DIN 53504 |
Lubrizol ESTANE® T5213 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
100% Modulus | 0.00630 GPa | 0.914 ksi | DIN 53504 |
Lubrizol ESTANE® 58564 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
100% Modulus | 0.00630 GPa | 0.914 ksi | ISO 37 |
AlphaGary Evoprene™ 032 Standard SBS Thermoplastic Elastomer Compound The Evoprene™ Standard is a styrene-butadiene -styrene based thermoplastic elastomer.Applications: extruded door, window and furniture seals and rubbing strips, mats, bump stops, grommets, coat han.. |
|||
100% Modulus | 0.00630 GPa | 0.914 ksi | Post cure 2 hours @ 232°C |
3M Dyneon™ FPO 3740 Fluoroelastomer 3M™ Dyneon™ FPO 3740 is a peroxide curable fluoroelastomer terpolymer containing 69.5 wt% fluorine. FPO 3740 can be used in compression, transfer or injection molding, and extrusion processes. Fea.. |
|||
100% Modulus | 0.00630 GPa | 0.914 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8605 (GF-S) Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued ** FormulationVTR 8605 |