Polymer Property : Tensile Creep Modulus, 1 hour = 1400 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1 hour	1400 - 2800 MPa	203000 - 406000 psi	Average value: 2130 MPa Grade Count:16
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim..
Tensile Creep Modulus, 1 hour	1400 - 2400 MPa	203000 - 348000 psi	Average value: 2120 MPa Grade Count:9
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an..
Tensile Creep Modulus, 1 hour	1400 MPa	203000 psi
Arkema Group Oroglas® DRM Acrylic, Extrusion Grade (discontinued **) OROGLAS DRM is an extrusion grade that offers the typical properties of high impact acrylic combined with matte surface finishing.OROGLAS DRM is recommended for extrusion of sheets for lighting, pr..
Tensile Creep Modulus, 1 hour	1400 MPa	203000 psi
Arkema Group Oroglas® DRT Acrylic, Impact Grade (discontinued **) For extrusion and injection molding applications. OROGLAS DRT combines good thermal resistance with an excellent impact resistance.Key features : impact resistance: up to 10 times more impact-resis..
Tensile Creep Modulus, 1 hour	1400 MPa	203000 psi
Arkema Group Oroglas® HFI-10 Acrylic, Impact Grade (discontinued **) OROGLAS HFI-10 is an impact grade that in addition to its superior impact resistance provides an improvement in flow which contribute to improve molding behavior and reduce cycle time.Key features :..
Tensile Creep Modulus, 1 hour	1400 MPa	203000 psi	ISO 899-1
Lanxess PocanÂ® S 1506 000000 PBT PBT, non-reinforced, injection molding extrusion, impact modified
Tensile Creep Modulus, 1 hour	1400 MPa @Time 3600 sec	203000 psi @Time 1.00 hour	50%RH; ISO 899-1
DuPont Performance Polymers Zytel® FG101L NC010 Nylon 66 (Unverified Data**) Unreinforced Polyamide 66 with Developed for Food Contact ApplicationsZytel FG101L NC010 is a lubricated polyamide 66 resin for injection molding. It has been developed for consideration into applic..
Tensile Creep Modulus, 1 hour	1400 MPa @Temperature 23.0 °C	203000 psi @Temperature 73.4 °F	50%RH; ISO 899
DuPont Performance Polymers Zytel® FG101L NC010 Nylon 66 (Unverified Data**) Zytel® FG101L NC010 is a lubricated polyamide 66 resin for injection molding. It has been developed for consideration into applications such as parts for the food industry.Information provided by D..
Tensile Creep Modulus, 1 hour	1400 - 2700 MPa	203000 - 392000 psi	Average value: 2350 MPa Grade Count:4
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate ..
Tensile Creep Modulus, 1 hour	1400 MPa	203000 psi
Arkema Group Oroglas® SG 10 Acrylic, Gamma Radiation Resistant (discontinued **) OROGLAS SG 10 is special Gamma - radiation - resistant formulation designed for use in medical devises.OROGLAS SG 10 maintains exceptional clarity after 5 megarads of Gamma radiation with no advers..
Tensile Creep Modulus, 1 hour	1400 MPa @Time 3600 sec	203000 psi @Time 1.00 hour	50%RH; ISO 899-1
DuPont Performance Polymers Zytel® 101F NC010 Nylon 66 (Unverified Data**) Unreinforced Polyamide 66Zytel 101F NC010 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont ..